John Eric Jones1, Qingsong Yu1, Meng Chen2. 1. a Department of Mechanical & Aerospace Engineering , Center for Surface Science and Plasma Technology, University of Missouri , Columbia , MO , USA. 2. b Nanova, Inc. , Columbia , MO , USA.
Abstract
Trimethylsilane (TMS) plasma nanocoatings were deposited onto stainless steel coupons in direct current (DC) and radio frequency (RF) glow discharges and additional NH3/O2 plasma treatment to tailor the coating surface properties. The chemical stability of the nanocoatings were evaluated after 12 week storage under dry condition (25 °C) and immersion in simulated body fluid (SBF) at 37 °C. It was found that nanocoatings did not impact surface roughness of underlying stainless steel substrates. X-ray photoelectron spectroscopy and Fourier transform infrared spectroscopy were used to characterize surface chemistry and compositions. Both DC and RF nanocoatings had Si- and C-rich composition; and the O- and N-contents on the surfaces were substantially increased after NH3/O2 plasma treatment. Contact angle measurements showed that DC-TMS nanocoating with NH3/O2 treatment generated very hydrophilic surfaces. DC-TMS nanocoatings with NH3/O2 treatment showed minimal surface chemistry change after 12 week immersion in SBF. However, nitrogen functionalities on RF-TMS coating with NH3/O2 post treatment were not as stable as in DC case. Cell culture studies revealed that the surfaces with DC coating and NH3/O2 post treatment demonstrated substantially improved proliferation of endothelial cells over the 12 week storage period at both dry and wet conditions, as compared to other coated surfaces. Therefore, DC nanocoatings with NH3/O2 post treatment may be chemically stable for long-term properties, including shelf-life storage and exposure to the bloodstream for coronary stent applications.
Trimethylsilane (n class="Chemical">TMS) plasma nanocoatings were deposited onto stainless steel coupons in direct current (DC) and radio frequency (RF) glow discharges and additional NH3/O2 plasma treatment to tailor the coating surface properties. The chemical stability of the nanocoatings were evaluated after 12 week storage under dry condition (25 °C) and immersion in simulated body fluid (SBF) at 37 °C. It was found that nanocoatings did not impact surface roughness of underlying stainless steel substrates. X-ray photoelectron spectroscopy and Fourier transform infrared spectroscopy were used to characterize surface chemistry and compositions. Both DC and RF nanocoatings had Si- and C-rich composition; and the O- and N-contents on the surfaces were substantially increased after NH3/O2 plasma treatment. Contact angle measurements showed that DC-TMS nanocoating with NH3/O2 treatment generated very hydrophilic surfaces. DC-TMS nanocoatings with NH3/O2 treatment showed minimal surface chemistry change after 12 week immersion in SBF. However, nitrogen functionalities on RF-TMS coating with NH3/O2 post treatment were not as stable as in DC case. Cell culture studies revealed that the surfaces with DC coating and NH3/O2 post treatment demonstrated substantially improved proliferation of endothelial cells over the 12 week storage period at both dry and wet conditions, as compared to other coated surfaces. Therefore, DC nanocoatings with NH3/O2 post treatment may be chemically stable for long-term properties, including shelf-life storage and exposure to the bloodstream for coronary stent applications.
Authors: Heinrich Wieneke; Thomas Sawitowski; Stephan Wnendt; Alfons Fischer; Olaf Dirsch; Ira Ariadne Karoussos; Raimund Erbel Journal: Herz Date: 2002-09 Impact factor: 1.443
Authors: Juan Luis Gutiérrez-Chico; Robert Jan van Geuns; Evelyn Regar; Willem J van der Giessen; Henning Kelbæk; Kari Saunamäki; Javier Escaned; Nieves Gonzalo; Carlo di Mario; Francesco Borgia; Eveline Nüesch; Héctor M García-García; Sigmund Silber; Stephan Windecker; Patrick W Serruys Journal: Eur Heart J Date: 2011-06-09 Impact factor: 29.983
Authors: Thithuha Phan; John E Jones; Meng Chen; Doug K Bowles; William P Fay; Qingsong Yu Journal: Materials (Basel) Date: 2022-08-29 Impact factor: 3.748