Comparison of Marginal Gap and Microleakage in Copy-Milled and Cad-Milled Zirconia Copings Bonded Using Light Cure and Chemical Cure Resin Bonding Systems.

This in vitro study assessed the marginal gap and marginal microleakage in zirconia copings fabricated using two computer aided techniques- CAD milling and Copy milling and cemented to respective tooth preparations using two resin bonding systems, light cure and self-cure resin bonding systems. 32 extracted premolars were prepared to receive zirconia copings fabricated using CAD/CAM and Copy milling techniques. Once the copings were fabricated, the samples were evaluated for marginal fit prior to cementation through microscopic observation. Evaluation of marginal gap was done again after cementation, in order to incorporate the influence of the resin bonding system on the marginal microgap. The specimens were evaluated under the stereomicroscope for micro-leakage using commercial software. A comparative statistical analysis was done following data collection using Mann-Whitney U test, Wilcoxon test and chi-square test. The data collected regarding marginal gap was well within 120 µ, which is in accordance with previous studies. However, Copy milled specimens showed statistically lesser marginal gap when compared to CAD milled specimens. While comparing microleakage, it was observed that the microleakage in Copy milled specimens bonded with light cure resin bonded cement was statistically lesser than that of specimens cemented with chemical cure resin cement.(P = 0.003). This in vitro study concluded that Copy milling technique fabricated zirconia restorations with lesser marginal gap and microleakage score in comparison to CAD milled samples. Light cure resin bonding system also proved to be more effective option compared to self cure resin bonding systems. However, the limitations of this study should be taken into concern and further research should be aimed at a larger sample size to validate the results.