STATEMENT OF PROBLEM: Zirconia cores are reported to be less translucent than glass, lithium disilicate, or alumina cores. This could affect the esthetic appearance and the clinical choices made when using zirconia-based restorations. PURPOSE: The purpose of this in vitro study was to evaluate the translucency of zirconia copings for single crowns fabricated using different CAD/CAM systems, using lithium disilicate glass ceramic as a control. MATERIAL AND METHODS: Using impressions made from a stainless steel complete-crown master die, 9 stone cast replicas were fabricated, numbered, and distributed into 8 ceramic ZrO(2) CAD/CAM system groups (Lava Frame 0.3 and 0.5, IPS e.max ZirCAD, VITA YZ, Procera AllZircon, Digizon, DC Zircon, and Cercon Base) and to a lithium disilicate glass-ceramic control group (IPS e.max Press) using a simple computer-generated randomization method. From each die, the manufacturer's authorized milling centers supplied 5 copings per group without applying any dying technique to the ceramic base material. The copings were prepared to allow for a 40-mum cement layer and were of different thicknesses according to system specifications. Translucency was measured by the direct transmission method with a digital photoradiometer mounted in a dark chamber. The light source was a 150-W halogen lamp beam. Measurements were repeated 3 times for each specimen. Data obtained were analyzed using 1-way ANOVA and the Bonferroni multiple comparison test (alpha=.05). RESULTS: Among ZrO(2) copings, Lava (0.3 mm and 0.5 mm thick) showed the highest (P<.05) values of translucency measured as light flow units (3.572 + or - 018 x 10(3) lx and 3.181 + or - 0.13 x 10(3) lx, respectively). These values represent 71.7% and 63.9%, respectively, of the glass-ceramic control group (4.98 x 10(3) lx). CONCLUSIONS: All ZrO(2) copings demonstrated different levels of light transmission, with the 2 Lava specimens showing the highest values. Translucency of zirconia copings was significantly lower (P=.001) than that of the lithium disilicate glass-ceramic control. Copyright 2010 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.
RCT Entities:
STATEMENT OF PROBLEM: Zirconia cores are reported to be less translucent than glass, lithium disilicate, or alumina cores. This could affect the esthetic appearance and the clinical choices made when using zirconia-based restorations. PURPOSE: The purpose of this in vitro study was to evaluate the translucency of zirconia copings for single crowns fabricated using different CAD/CAM systems, using lithium disilicate glass ceramic as a control. MATERIAL AND METHODS: Using impressions made from a stainless steel complete-crown master die, 9 stone cast replicas were fabricated, numbered, and distributed into 8 ceramic ZrO(2) CAD/CAM system groups (Lava Frame 0.3 and 0.5, IPS e.max ZirCAD, VITA YZ, Procera AllZircon, Digizon, DC Zircon, and Cercon Base) and to a lithium disilicate glass-ceramic control group (IPS e.max Press) using a simple computer-generated randomization method. From each die, the manufacturer's authorized milling centers supplied 5 copings per group without applying any dying technique to the ceramic base material. The copings were prepared to allow for a 40-mum cement layer and were of different thicknesses according to system specifications. Translucency was measured by the direct transmission method with a digital photoradiometer mounted in a dark chamber. The light source was a 150-W halogen lamp beam. Measurements were repeated 3 times for each specimen. Data obtained were analyzed using 1-way ANOVA and the Bonferroni multiple comparison test (alpha=.05). RESULTS: Among ZrO(2) copings, Lava (0.3 mm and 0.5 mm thick) showed the highest (P<.05) values of translucency measured as light flow units (3.572 + or - 018 x 10(3) lx and 3.181 + or - 0.13 x 10(3) lx, respectively). These values represent 71.7% and 63.9%, respectively, of the glass-ceramic control group (4.98 x 10(3) lx). CONCLUSIONS: All ZrO(2) copings demonstrated different levels of light transmission, with the 2 Lava specimens showing the highest values. Translucency of zirconia copings was significantly lower (P=.001) than that of the lithium disilicate glass-ceramic control. Copyright 2010 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.
Authors: J F Esquivel-Upshaw; M J Kim; S M Hsu; N Abdulhameed; R Jenkins; D Neal; F Ren; A E Clark Journal: J Dent Date: 2017-10-16 Impact factor: 4.379
Authors: Markus Wertz; Florian Fuchs; Hieronymus Hoelzig; Julia Maria Wertz; Gert Kloess; Sebastian Hahnel; Martin Rosentritt; Andreas Koenig Journal: Materials (Basel) Date: 2021-04-22 Impact factor: 3.623