Effect of acetabular cup abduction angle on wear of ultrahigh-molecular-weight polyethylene in hip simulator testing.

The effect of acetabular component positioning on the wear rates of metal-on-polyethylene articulations has not been extensively studied. Placement of acetabular cups at abduction angles of more than 40° has been noted as a possible reason for early failure caused by increased wear. We conducted a study to evaluate the effects of different acetabular cup abduction angles on polyethylene wear rate, wear area, contact pressure, and contact area. Our in vitro study used a hip joint simulator and finite element analysis to assess the effects of cup orientation at 4 angles (0°, 40°, 50°, 70°) on wear and contact properties. Polyethylene bearings with 28-mm cobalt-chrome femoral heads were cycled in an environment mimicking in vivo joint fluid to determine the volumetric wear rate after 10 million cycles. Contact pressure and contact area for each cup abduction angle were assessed using finite element analysis. Results were correlated with cup abduction angles to determine if there were any differences among the 4 groups. The inverse relationship between volumetric wear rate and acetabular cup inclination angle demonstrated less wear with steeper cup angles. The largest abduction angle (70°) had the lowest contact area, largest contact pressure, and smallest head coverage. Conversely, the smallest abduction angle (0°) had the most wear and most head coverage. Polyethylene wear after total hip arthroplasty is a major cause of osteolysis and aseptic loosening, which may lead to premature implant failure. Several studies have found that high wear rates for cups oriented at steep angles contributed to their failure. Our data demonstrated that larger cup abduction angles were associated with lower, not higher, wear. However, this potentially "protective" effect is likely counteracted by other complications of steep cup angles, including impingement, instability, and edge loading. These factors may be more relevant in explaining why implants fail at a higher rate if cups are oriented at more than 40° of abduction.