PURPOSES: This study evaluated the effect of gamma radiation on the microtensile bond strength of resin-based composite restoration to human enamel and dentin performed either before or after radiotherapy. METHODS: Thirty sound human third molars were sectioned mesio-distally into buccal and lingual halves and then randomly divided into enamel or dentin groups. Enamel and dentin substrates were randomly divided into three sub-groups (n = 10): Control, which received no irradiation; specimens were irradiated before restoration protocol; and specimens were irradiated after restoration protocol. Radiation therapy was defined by application of 60-Gy dose fractionally with daily exposures of 2 Gy, 5 days a week, over 6 weeks. Restorations were carried out using Adper Single Bond adhesive system and Filtek Z250 resin composite. The specimens were sectioned producing 4 sticks per specimen and submitted to microtensile on a testing machine. Data were submitted to two-way ANOVA followed by Tukey test (p < 0.05). Failure modes were examined under optical microscopy and SEM. RESULTS: Bond strength to enamel was significantly higher than to dentin irrespective radiation therapy. Radiotherapy applied before restoration significantly reduced the bond strength to both substrates. A predominance of adhesive failures was detected for control groups and groups restored before radiotherapy. Cohesive failures in dentin and enamel increased when the specimens were restored after irradiation. CONCLUSIONS: The gamma radiation had a significant detrimental effect on bond strength to human enamel and dentin when the adhesive restorative procedure was carried out after radiotherapy.
PURPOSES: This study evaluated the effect of gamma radiation on the microtensile bond strength of resin-based composite restoration to human enamel and dentin performed either before or after radiotherapy. METHODS: Thirty sound human third molars were sectioned mesio-distally into buccal and lingual halves and then randomly divided into enamel or dentin groups. Enamel and dentin substrates were randomly divided into three sub-groups (n = 10): Control, which received no irradiation; specimens were irradiated before restoration protocol; and specimens were irradiated after restoration protocol. Radiation therapy was defined by application of 60-Gy dose fractionally with daily exposures of 2 Gy, 5 days a week, over 6 weeks. Restorations were carried out using Adper Single Bond adhesive system and Filtek Z250 resin composite. The specimens were sectioned producing 4 sticks per specimen and submitted to microtensile on a testing machine. Data were submitted to two-way ANOVA followed by Tukey test (p < 0.05). Failure modes were examined under optical microscopy and SEM. RESULTS: Bond strength to enamel was significantly higher than to dentin irrespective radiation therapy. Radiotherapy applied before restoration significantly reduced the bond strength to both substrates. A predominance of adhesive failures was detected for control groups and groups restored before radiotherapy. Cohesive failures in dentin and enamel increased when the specimens were restored after irradiation. CONCLUSIONS: The gamma radiation had a significant detrimental effect on bond strength to human enamel and dentin when the adhesive restorative procedure was carried out after radiotherapy.
Authors: Maria Stella Raffaini; Jaciara Miranda Gomes-Silva; Carolina Paes Torres-Mantovani; Regina Guenka Palma-Dibb; Maria Cristina Borsatto Journal: Am J Dent Date: 2008-06 Impact factor: 1.522
Authors: Rowida Abdalla; Maha A Niazy; Wael E Jamil; Hala A Hazzaa; Amal A Elbatouti Journal: Radiat Environ Biophys Date: 2017-03-23 Impact factor: 1.925
Authors: Roberta Galetti; Alan Roger Santos-Silva; Alberto Nogueira da Gama Antunes; Fabio de Abreu Alves; Marcio Ajudarte Lopes; Mario Fernando de Goes Journal: Clin Oral Investig Date: 2013-12-06 Impact factor: 3.573
Authors: Juliana Arid; Regina Guenka Palma-Dibb; Harley Francisco de Oliveira; Paulo Nelson-Filho; Fabricio Kitazono de Carvalho; Lea Assed Bezerra da Silva; Talitha de Siqueira Mellara; Raquel Assed Bezerra da Silva; Juliana Jendiroba Faraoni; Alexandra Mussolino de Queiroz Journal: Support Care Cancer Date: 2019-04-24 Impact factor: 3.603