Elif Delve Başer Can1, Güher Barut2, Vasfiye Işık3, Emriye Algül4, Gökhan Yaprak5, Esra Can6. 1. Department of Endodontics, Yeditepe University Faculty of Dentistry, Bağdat Cad. No: 238 Göztepe, Kadıköy, Istanbul, Turkey. elif.baser@yeditepe.edu.tr. 2. Department of Endodontics, Yeditepe University Faculty of Dentistry, Bağdat Cad. No: 238 Göztepe, Kadıköy, Istanbul, Turkey. 3. Department of Endodontics, Istanbul Health and Technology University Faculty of Dentistry, Istanbul, Turkey. 4. Department of Radiation Oncology, Istanbul Kartal Dr. Lutfi Kirdar City Hospital, Ministry of Health, Sağlık Bilimleri University, Istanbul, Turkey. 5. Department of Radiation Oncology, Sağlık Bilimleri University, Istanbul, Turkey. 6. Department of Restorative Dentistry, Yeditepe University Faculty of Dentistry, Istanbul, Turkey.
Abstract
OBJECTIVES: The aim of this study is to evaluate the influence of ionizing radiotherapy on the resin-dentin interface in endodontically treated teeth restored with fiber posts using a dual-cure resin cement performed with the etch-and-rinse (ER) and self-etch (SE) approaches in terms of push-out bond strength (MPa), and to analyze the post/cement/dentin interface using scanning electron microscopy (SEM). MATERIALS AND METHODS: Seventy-six single-rooted human teeth were used and randomly assigned into two main groups (n = 38): one non-irradiated group (NoRad) and one group subjected to a cumulative radiation dose of 60 Gy (Rad). All root canals were instrumented and were further subdivided into two subgroups (n = 19) following the adhesive approach: ER (RadER; NoRadER) and SE (RadSE; NoRadSE) used for fiber post luting with the universal adhesive and dual cure resin cement. Each root was sectioned perpendicularly to its long axis and sections from the middle third of the roots were chosen for SEM analysis and push-out bond strength test. Two-way ANOVA with post hoc Tukey tests and a dummy variable linear regression analysis were used for data analysis. RESULTS: Regardless of the adhesive approach, push-out bond strength in irradiated teeth resulted in significantly lower values than non-irradiated teeth (p = 0.0001). There were no significant differences between the ER and SE approaches in non-irradiated teeth (p = 0.955), whereas the ER approach showed significantly higher bond strengths than the SE approach in irradiated teeth (p = 0.0001). CONCLUSIONS: Ionizing radiotherapy resulted in dentin structure disruption and negatively affected the push-out bond strength of fiber posts to intraradicular dentin. The reduction in bond strength was also more significant with the SE approach than with the ER approach. CLINICAL RELEVANCE: The alterations resulting from root dentin irradiation seem to influence adhesive systems bond strength to dentin, as these changes contribute to lower push-out bond strength in irradiated groups before fiber post luting. Thus, clinicians should prepare patients with a reasonable restorative treatment plan prior to radiotherapy and simultaneously initiate a preventive program during radiotherapy.
OBJECTIVES: The aim of this study is to evaluate the influence of ionizing radiotherapy on the resin-dentin interface in endodontically treated teeth restored with fiber posts using a dual-cure resin cement performed with the etch-and-rinse (ER) and self-etch (SE) approaches in terms of push-out bond strength (MPa), and to analyze the post/cement/dentin interface using scanning electron microscopy (SEM). MATERIALS AND METHODS: Seventy-six single-rooted human teeth were used and randomly assigned into two main groups (n = 38): one non-irradiated group (NoRad) and one group subjected to a cumulative radiation dose of 60 Gy (Rad). All root canals were instrumented and were further subdivided into two subgroups (n = 19) following the adhesive approach: ER (RadER; NoRadER) and SE (RadSE; NoRadSE) used for fiber post luting with the universal adhesive and dual cure resin cement. Each root was sectioned perpendicularly to its long axis and sections from the middle third of the roots were chosen for SEM analysis and push-out bond strength test. Two-way ANOVA with post hoc Tukey tests and a dummy variable linear regression analysis were used for data analysis. RESULTS: Regardless of the adhesive approach, push-out bond strength in irradiated teeth resulted in significantly lower values than non-irradiated teeth (p = 0.0001). There were no significant differences between the ER and SE approaches in non-irradiated teeth (p = 0.955), whereas the ER approach showed significantly higher bond strengths than the SE approach in irradiated teeth (p = 0.0001). CONCLUSIONS: Ionizing radiotherapy resulted in dentin structure disruption and negatively affected the push-out bond strength of fiber posts to intraradicular dentin. The reduction in bond strength was also more significant with the SE approach than with the ER approach. CLINICAL RELEVANCE: The alterations resulting from root dentin irradiation seem to influence adhesive systems bond strength to dentin, as these changes contribute to lower push-out bond strength in irradiated groups before fiber post luting. Thus, clinicians should prepare patients with a reasonable restorative treatment plan prior to radiotherapy and simultaneously initiate a preventive program during radiotherapy.
Authors: Catherine H L Hong; Joel J Napeñas; Brian D Hodgson; Monique A Stokman; Vickie Mathers-Stauffer; Linda S Elting; Fred K L Spijkervet; Michael T Brennan Journal: Support Care Cancer Date: 2010-05-07 Impact factor: 3.603
Authors: Jacques Ferlay; Isabelle Soerjomataram; Rajesh Dikshit; Sultan Eser; Colin Mathers; Marise Rebelo; Donald Maxwell Parkin; David Forman; Freddie Bray Journal: Int J Cancer Date: 2014-10-09 Impact factor: 7.396