AIM: To test the hypothesis that peri-implant bone formation and mechanical stability of surface-modified zirconia and titanium implants are equivalent. MATERIALS AND METHODS: Twelve minipigs received three types of implants on either side of the mandible 8 weeks after removal of all pre-molar teeth: (i) a zirconia implant with a sandblasted surface; (ii) a zirconia implants with a sandblasted and etched surface; and (iii) a titanium implant with a sandblasted and acid-etched surface that served as a control. Removal torque and peri-implant bone regeneration were evaluated in six animals each after 4 and 13 weeks. RESULTS: The titanium surface was significantly rougher than both tested zirconia surfaces. Mean bone to implant contact (BIC) did not differ significantly between the three implant types after 4 weeks but was significantly higher for titanium compared with both zirconia implants after 13 weeks (p<0.05). Bone volume density (BVD) did not differ significantly at any interval. Removal torque was significantly higher for titanium compared with both zirconia surfaces after 4 and 13 weeks (p<0.001). The sandblasted and etched zirconia surface showed a significantly higher removal torque after 4 weeks compared with sandblasted zirconia (p<0.05); this difference levelled out after 13 weeks. CONCLUSIONS: It is concluded that all implants achieved osseointegration with similar degrees of BIC and BVD; however, titanium implants showed a higher resistance to removal torque, probably due to higher surface roughness.
AIM: To test the hypothesis that peri-implant bone formation and mechanical stability of surface-modified zirconia and titanium implants are equivalent. MATERIALS AND METHODS: Twelve minipigs received three types of implants on either side of the mandible 8 weeks after removal of all pre-molar teeth: (i) a zirconia implant with a sandblasted surface; (ii) a zirconia implants with a sandblasted and etched surface; and (iii) a titanium implant with a sandblasted and acid-etched surface that served as a control. Removal torque and peri-implant bone regeneration were evaluated in six animals each after 4 and 13 weeks. RESULTS: The titanium surface was significantly rougher than both tested zirconia surfaces. Mean bone to implant contact (BIC) did not differ significantly between the three implant types after 4 weeks but was significantly higher for titanium compared with both zirconia implants after 13 weeks (p<0.05). Bone volume density (BVD) did not differ significantly at any interval. Removal torque was significantly higher for titanium compared with both zirconia surfaces after 4 and 13 weeks (p<0.001). The sandblasted and etched zirconia surface showed a significantly higher removal torque after 4 weeks compared with sandblasted zirconia (p<0.05); this difference levelled out after 13 weeks. CONCLUSIONS: It is concluded that all implants achieved osseointegration with similar degrees of BIC and BVD; however, titanium implants showed a higher resistance to removal torque, probably due to higher surface roughness.
Authors: Fernanda H Schünemann; María E Galárraga-Vinueza; Ricardo Magini; Márcio Fredel; Filipe Silva; Júlio C M Souza; Yu Zhang; Bruno Henriques Journal: Mater Sci Eng C Mater Biol Appl Date: 2019-01-16 Impact factor: 7.328
Authors: Welson Cunha; Oscar Carvalho; Bruno Henriques; Filipe S Silva; Mutlu Özcan; Júlio C M Souza Journal: Lasers Med Sci Date: 2022-01-13 Impact factor: 3.161