AIM: To evaluate the effect of repeated sterilization cycles in dry oven or autoclave, on the mechanical behaviour and fatigue resistance of rotary endodontic Ni-Ti instruments. METHODOLOGY: New Ni-Ti instruments were subjected to five consecutive sterilization cycles in a dry oven or steam autoclave. Microhardness was measured in the nonmachined parts of the shanks of instruments using a Vickers indenter. Specimens of Ni-Ti wires were submitted to the same sterilization protocol and tensile tested until rupture. A group of instruments were fatigued to one half of their average fatigue life and then sterilized. New and sterilized instruments were fatigue tested until rupture. anova tests at alpha = 0.05 were used for statistical analysis. RESULTS: Sterilization procedures resulted in no significant changes in Vickers microhardness, nor in the parameters describing the mechanical behaviour of the wires. However, the number of cycles to failure was statistically higher for all instruments after dry heat or autoclave sterilization cycles. In the instruments previously fatigued to one half of their fatigue life, autoclave sterilization gave rise to an increase of 39% in the remaining number of cycles to failure. CONCLUSIONS: Changes in the mechanical properties of Ni-Ti endodontic instruments after five cycles of commonly used sterilization procedures were insignificant. The sterilization procedures are safe as they produced a significant increase in the fatigue resistance of the instruments.
AIM: To evaluate the effect of repeated sterilization cycles in dry oven or autoclave, on the mechanical behaviour and fatigue resistance of rotary endodontic Ni-Ti instruments. METHODOLOGY: New Ni-Ti instruments were subjected to five consecutive sterilization cycles in a dry oven or steam autoclave. Microhardness was measured in the nonmachined parts of the shanks of instruments using a Vickers indenter. Specimens of Ni-Ti wires were submitted to the same sterilization protocol and tensile tested until rupture. A group of instruments were fatigued to one half of their average fatigue life and then sterilized. New and sterilized instruments were fatigue tested until rupture. anova tests at alpha = 0.05 were used for statistical analysis. RESULTS: Sterilization procedures resulted in no significant changes in Vickers microhardness, nor in the parameters describing the mechanical behaviour of the wires. However, the number of cycles to failure was statistically higher for all instruments after dry heat or autoclave sterilization cycles. In the instruments previously fatigued to one half of their fatigue life, autoclave sterilization gave rise to an increase of 39% in the remaining number of cycles to failure. CONCLUSIONS: Changes in the mechanical properties of Ni-Ti endodontic instruments after five cycles of commonly used sterilization procedures were insignificant. The sterilization procedures are safe as they produced a significant increase in the fatigue resistance of the instruments.
Authors: Felipe Augusto Restrepo-Restrepo; Viviana Andrea Holguín-Vásquez; Syldana Julieth Cañas-Jiménez; Paula Andrea Villa-Machado; Sara Ochoa-Soto; Claudia Patricia Ossa-Orozco; Sergio Iván Tobón-Arroyave Journal: Dent Res J (Isfahan) Date: 2021-06-22