Introduction: This study aimed to determine the bond strength of fiber post to composite core following surface treatment with Er,Cr:YSGG laser at different powers and sandblasting with and without thermocycling. Methods: In this experimental study, 30 fiber posts (Glassix, Nordin, Switzerland) were randomly divided into 5 groups of sandblasting, no treatment and laser irradiation at 1, 1.5 and 2 W powers. Following composite filling and mounting, 1-mm thick sections were made for pushout bond strength testing. Half of the samples in each group were subjected to thermocycling (n=15). Two-way analysis of variance (ANOVA) was used to analyze the bond strength values. Pairwise comparisons were made using Tukey test (P<0.05). Results: Effect of treatment method on push-out bond strength of fiber post to composite core was significant (P=0.017), while thermocycling had no significant effect on bond strength (P=0.964). Pairwise comparison of surface treatment methods revealed no significant difference in groups with and without thermocycling (P>0.05), but Er,Cr:YSGG laser irradiation with 1 W power yielded significantly higher bond strength than the control group (P=0.01). Conclusion:Irradiation of Er,Cr:YSGG laser at 1 W power increased the bond strength of fiber post to composite core. Thermocycling slightly decreased the bond strength at the fiber postcore interface.
RCT Entities:
Introduction: This study aimed to determine the bond strength of fiber post to composite core following surface treatment with Er,Cr:YSGG laser at different powers and sandblasting with and without thermocycling. Methods: In this experimental study, 30 fiber posts (Glassix, Nordin, Switzerland) were randomly divided into 5 groups of sandblasting, no treatment and laser irradiation at 1, 1.5 and 2 W powers. Following composite filling and mounting, 1-mm thick sections were made for pushout bond strength testing. Half of the samples in each group were subjected to thermocycling (n=15). Two-way analysis of variance (ANOVA) was used to analyze the bond strength values. Pairwise comparisons were made using Tukey test (P<0.05). Results: Effect of treatment method on push-out bond strength of fiber post to composite core was significant (P=0.017), while thermocycling had no significant effect on bond strength (P=0.964). Pairwise comparison of surface treatment methods revealed no significant difference in groups with and without thermocycling (P>0.05), but Er,Cr:YSGG laser irradiation with 1 W power yielded significantly higher bond strength than the control group (P=0.01). Conclusion: Irradiation of Er,Cr:YSGG laser at 1 W power increased the bond strength of fiber post to composite core. Thermocycling slightly decreased the bond strength at the fiber postcore interface.
Keywords:
Bond strength; Composite; Cr:YSGG laser; Er; Post
Authors: Cecilia Goracci; Andrea Urbano Tavares; Andrea Fabianelli; Francesca Monticelli; Ornella Raffaelli; Paulo Capel Cardoso; Franklin Tay; Marco Ferrari Journal: Eur J Oral Sci Date: 2004-08 Impact factor: 2.612