A D Uygun1, E Kol1, M K C Topcu1, F Seckin1, I Ersoy2, M Tanriver3. 1. Department of Endodontics, Faculty of Dentistry, Ataturk University, Erzurum, Turkey. 2. Department of Endodontics, Faculty of Dentistry, Sifa University, Izmir, Turkey. 3. Department of Pedodontics, Faculty of Dentistry, Sifa University, Izmir, Turkey.
Abstract
AIM: To compare the cyclic fatigue resistance of ProTaper Gold (PTG, Dentsply Tulsa Dental Specialities, Tulsa, OK, USA), ProTaper Next (PTN, Dentsply Tulsa Dental Specialities) and ProTaper Universal (PTU, Dentsply Tulsa Dental Specialities) instruments at different levels. METHODOLOGY: A total of 72 files were used to evaluate the cyclic fatigue of PTU (F2), PTN (X2) and PTG (F2) at 5 mm (n = 12) and 8 mm (n = 12) from the tip in 3-mm-radius steel canals with a 60° angle of curvature. The time to fracture was recorded. The Kolmogorov-Smirnov test was used to assess the normality of the samples distribution, and the statistical analysis was performed using the independent sample t-test (P < 0.01). RESULTS: Significant differences were found amongst the instruments 5 mm from the tip (P < 0.01). The PTG files had the highest CF resistance, and the PTN files displayed greater CF resistance than the PTU files. No significant differences were found between the PTG and PTN files 8 mm from the tip (P > 0.01). The PTG and PTN files demonstrated greater CF resistance than the PTU files (P < 0.01). CONCLUSIONS: The PTG instruments were the most resistant 5 and 8 mm from the tip; however, at 8 mm, there was no difference between the PTG and PTN instruments. The PTU files had the lowest CF resistance at all levels.
AIM: To compare the cyclic fatigue resistance of ProTaper Gold (PTG, Dentsply Tulsa Dental Specialities, Tulsa, OK, USA), ProTaper Next (PTN, Dentsply Tulsa Dental Specialities) and ProTaper Universal (PTU, Dentsply Tulsa Dental Specialities) instruments at different levels. METHODOLOGY: A total of 72 files were used to evaluate the cyclic fatigue of PTU (F2), PTN (X2) and PTG (F2) at 5 mm (n = 12) and 8 mm (n = 12) from the tip in 3-mm-radius steel canals with a 60° angle of curvature. The time to fracture was recorded. The Kolmogorov-Smirnov test was used to assess the normality of the samples distribution, and the statistical analysis was performed using the independent sample t-test (P < 0.01). RESULTS: Significant differences were found amongst the instruments 5 mm from the tip (P < 0.01). The PTG files had the highest CF resistance, and the PTN files displayed greater CF resistance than the PTU files. No significant differences were found between the PTG and PTN files 8 mm from the tip (P > 0.01). The PTG and PTN files demonstrated greater CF resistance than the PTU files (P < 0.01). CONCLUSIONS: The PTG instruments were the most resistant 5 and 8 mm from the tip; however, at 8 mm, there was no difference between the PTG and PTN instruments. The PTU files had the lowest CF resistance at all levels.
Authors: Ludmila Smith de Jesus Oliveira; Rafaella Mariana Fontes de Bragança; Rafael Sarkis-Onofre; André Luis Faria-E-Silva Journal: Restor Dent Endod Date: 2021-06-18
Authors: Abdullah Alqedairi; Hussam Alfawaz; Bader Abualjadayel; Mohammad Alanazi; Ahmad Alkhalifah; Ahmed Jamleh Journal: BMC Oral Health Date: 2019-06-21 Impact factor: 2.757