OBJECTIVES: The aim of this study was to evaluate the setting characteristics of low-shrinking resin composites and examine the possible interactions with curing efficiency and marginal adaptation in dentin cavities. METHODS: The materials tested were Ceram X Mono/CM, Premise/PR, Clearfil Majesty/CM, ELS/EL, and Filtek Silorane/FS. Polymerization shrinkage strain (%S), strain rate (%S(r)) and time at maximum strain rate (t(max)) were measured using the bonded disk method. Curing efficiency was measured on the top and bottom surfaces of composites with ATR-FTIR spectroscopy. Marginal adaptation was measured in unbonded (%VVF) and bonded (%XVF) specimens by computerized X-ray microtomography (micro-XCT). The % linear length of the interfacial gaps along the cavity margins (%LD) and the maximum gap width (WD(max)) were calculated under optical microscopy on sectioned specimens. Statistical analysis was performed with one- and two-way ANOVA, Bonferroni's post hoc test and Pearson's correlation coefficient. RESULTS: The %S values ranged from 1.34% (FS) to 2.29% (CX), while %S(r) ranged from 0.06%s(-1) (FS) to 0.15%s(-1) (CX). %VVF values extended from 1.9% (FS) to 5.3% (CX) and for %XVF from 1.98% (FS) to 3.35% (CX). The values for %LD ranged from 36.52% (FS) to 81.28% (CX). Linear regression showed strong positive correlation for %S(r) and t(max) with %VVF (r(2)=0.884 and r(2)=0.927) and also for %S(r) and t(max) with %LD (r(2)=0.823 and r(2)=0.869). SIGNIFICANCE: %S(r) and t(max) are more representative than %S in determining the setting pattern of the materials and are strongly correlated to marginal adaptation. The silorane material showed better behavior than the dimethacrylate materials in setting shrinkage and marginal adaptation.
OBJECTIVES: The aim of this study was to evaluate the setting characteristics of low-shrinking resin composites and examine the possible interactions with curing efficiency and marginal adaptation in dentin cavities. METHODS: The materials tested were Ceram X Mono/CM, Premise/PR, Clearfil Majesty/CM, ELS/EL, and Filtek Silorane/FS. Polymerization shrinkage strain (%S), strain rate (%S(r)) and time at maximum strain rate (t(max)) were measured using the bonded disk method. Curing efficiency was measured on the top and bottom surfaces of composites with ATR-FTIR spectroscopy. Marginal adaptation was measured in unbonded (%VVF) and bonded (%XVF) specimens by computerized X-ray microtomography (micro-XCT). The % linear length of the interfacial gaps along the cavity margins (%LD) and the maximum gap width (WD(max)) were calculated under optical microscopy on sectioned specimens. Statistical analysis was performed with one- and two-way ANOVA, Bonferroni's post hoc test and Pearson's correlation coefficient. RESULTS: The %S values ranged from 1.34% (FS) to 2.29% (CX), while %S(r) ranged from 0.06%s(-1) (FS) to 0.15%s(-1) (CX). %VVF values extended from 1.9% (FS) to 5.3% (CX) and for %XVF from 1.98% (FS) to 3.35% (CX). The values for %LD ranged from 36.52% (FS) to 81.28% (CX). Linear regression showed strong positive correlation for %S(r) and t(max) with %VVF (r(2)=0.884 and r(2)=0.927) and also for %S(r) and t(max) with %LD (r(2)=0.823 and r(2)=0.869). SIGNIFICANCE: %S(r) and t(max) are more representative than %S in determining the setting pattern of the materials and are strongly correlated to marginal adaptation. The silorane material showed better behavior than the dimethacrylate materials in setting shrinkage and marginal adaptation.
Authors: Renata Kirita Doi Sampaio; Linda Wang; Rodrigo Varella de Carvalho; Eugenio José Garcia; Andréa Mello de Andrade; Celso Afonso Klein-Júnior; Rosa Helena Miranda Grande; Sandra Kiss Moura Journal: J Appl Oral Sci Date: 2013 Jan-Feb Impact factor: 2.698