Sillas Duarte1, Jin-Ho Phark, Fabiana Mansur Varjão, Avishai Sadan. 1. Department of Comprehensive Care, Case Western Reserve University, School of Dental Medicine, 10900 Euclid Avenue, Cleveland, OH 44106-4905, USA. sillas.duarte@case.edu
Abstract
OBJECTIVES: To study the microtensile bond strengths and nanoleakage of low-shrinkage composite to dentin. The null hypotheses tested were (1) aging does not affect the bonding of low-shrinkage composite; (2) there is no difference in microtensile bond strengths and nanoleakage using different bonding strategies. METHODS: 32 extracted molars were assigned to one of four groups: LS System Adhesive (LS, 3M ESPE); dentin etched for 15s with phosphoric acid+LS System Adhesive (LSpa); Adper Single Bond Plus (SB, 3M ESPE); SB+LS Bond (SBLS). Occlusal dentin was exposed and restored with Filtek LS (3M ESPE). The samples were tested after 24h or after 20,000 thermocycles and 6 months of aging. Teeth were sectioned with a cross-section of 0.8+/-0.2mm(2) and fractured at a crosshead speed of 1mm/min. The data were submitted to ANOVA/Duncan's post hoc test, at p<0.05. Five slabs from each group were selected and immersed in 50wt% ammoniacal silver nitrate. Then, specimens were processed for SEM, the silver penetration was measured and data analyzed with Kruskal-Wallis at p<0.05. RESULTS: No statistically significant difference was found among the experimental groups for the factor dentin treatment (p=0.165) and aging (p=0.091). All experimental groups exhibit some degree of nanoleakage. There was no adhesion of Filtek LS applied directly over dentin surfaces treated with SB. SIGNIFICANCE: The new low-shrinkage resin composite showed compatibility only with its dedicated adhesive. Pre-etching did not improve the bond strengths to low-shrinkage resin composite. Some degree of nanoleakage was evident in all groups.
OBJECTIVES: To study the microtensile bond strengths and nanoleakage of low-shrinkage composite to dentin. The null hypotheses tested were (1) aging does not affect the bonding of low-shrinkage composite; (2) there is no difference in microtensile bond strengths and nanoleakage using different bonding strategies. METHODS: 32 extracted molars were assigned to one of four groups: LS System Adhesive (LS, 3M ESPE); dentin etched for 15s with phosphoric acid+LS System Adhesive (LSpa); Adper Single Bond Plus (SB, 3M ESPE); SB+LS Bond (SBLS). Occlusal dentin was exposed and restored with Filtek LS (3M ESPE). The samples were tested after 24h or after 20,000 thermocycles and 6 months of aging. Teeth were sectioned with a cross-section of 0.8+/-0.2mm(2) and fractured at a crosshead speed of 1mm/min. The data were submitted to ANOVA/Duncan's post hoc test, at p<0.05. Five slabs from each group were selected and immersed in 50wt% ammoniacal silver nitrate. Then, specimens were processed for SEM, the silver penetration was measured and data analyzed with Kruskal-Wallis at p<0.05. RESULTS: No statistically significant difference was found among the experimental groups for the factor dentin treatment (p=0.165) and aging (p=0.091). All experimental groups exhibit some degree of nanoleakage. There was no adhesion of Filtek LS applied directly over dentin surfaces treated with SB. SIGNIFICANCE: The new low-shrinkage resin composite showed compatibility only with its dedicated adhesive. Pre-etching did not improve the bond strengths to low-shrinkage resin composite. Some degree of nanoleakage was evident in all groups.
Authors: Bruno Baracco; M Victoria Fuentes; Miguel A Garrido; Santiago González-López; Laura Ceballos Journal: Odontology Date: 2012-07-13 Impact factor: 2.634
Authors: Kelli A Agee; Anuradha Prakki; Tariq Abu-Haimed; Ghada H Naguib; Manar Abu Nawareg; Arzu Tezvergil-Mutluay; Debora L S Scheffel; Chen Chen; Seung Soon Jang; Hyea Hwang; Martha Brackett; Geneviéve Grégoire; Franklin R Tay; Lorenzo Breschi; David H Pashley Journal: Dent Mater Date: 2015-01-19 Impact factor: 5.304
Authors: Ebtehal G Albeshir; Rashed Alsahafi; Reem Albluwi; Abdulrahman A Balhaddad; Heba Mitwalli; Thomas W Oates; Gary D Hack; Jirun Sun; Michael D Weir; Hockin H K Xu Journal: Materials (Basel) Date: 2022-04-18 Impact factor: 3.748
Authors: Renata Kirita Doi Sampaio; Linda Wang; Rodrigo Varella de Carvalho; Eugenio José Garcia; Andréa Mello de Andrade; Celso Afonso Klein-Júnior; Rosa Helena Miranda Grande; Sandra Kiss Moura Journal: J Appl Oral Sci Date: 2013 Jan-Feb Impact factor: 2.698