PURPOSE: The aim of this study was to evaluate bone apposition to a modified sandblasted and acid-etched (SLA) implant surface (modSLA) in the canine mandible as compared with the standard SLA surface. MATERIAL AND METHODS: In this experimental study, all mandibular premolars and first molars were extracted bilaterally in five foxhounds. After a healing period of 6 months, each side of the mandible received six randomly assigned dental implants alternating between the standard SLA and modSLA surface. The dogs were sacrificed at 2 weeks (n=2) or 4 weeks (n=3) after implant placement. Histologic and histomorphometric analyses were then performed for each implant. RESULTS: The microscopic healing patterns at weeks 2 and 4 for the two implant types with the standard SLA and modSLA surfaces showed similar qualitative findings. New bone tissue had already established direct contact with implant surfaces after 2 weeks of healing. The mean percentage of newly formed bone in contact with the implant (BIC) was significantly greater for modSLA (28.2+/-7.9%) than for SLA (22.2+/-7.3%) (P<0.05). This difference was no longer evident after 4 weeks. An increase in BIC for both implant surface types occurred from weeks 2 to 4. This increase was statistically significant when compared with SLA at 2 weeks (P<0.05), but not when compared with modSLA at 2 weeks. CONCLUSION: The data from the present study demonstrate significantly more bone apposition for the modSLA surface than the standard SLA surface after 2 weeks of healing. This increased bone apposition may allow a further reduction of the healing period following implant placement for patients undergoing early loading procedures.
PURPOSE: The aim of this study was to evaluate bone apposition to a modified sandblasted and acid-etched (SLA) implant surface (modSLA) in the canine mandible as compared with the standard SLA surface. MATERIAL AND METHODS: In this experimental study, all mandibular premolars and first molars were extracted bilaterally in five foxhounds. After a healing period of 6 months, each side of the mandible received six randomly assigned dental implants alternating between the standard SLA and modSLA surface. The dogs were sacrificed at 2 weeks (n=2) or 4 weeks (n=3) after implant placement. Histologic and histomorphometric analyses were then performed for each implant. RESULTS: The microscopic healing patterns at weeks 2 and 4 for the two implant types with the standard SLA and modSLA surfaces showed similar qualitative findings. New bone tissue had already established direct contact with implant surfaces after 2 weeks of healing. The mean percentage of newly formed bone in contact with the implant (BIC) was significantly greater for modSLA (28.2+/-7.9%) than for SLA (22.2+/-7.3%) (P<0.05). This difference was no longer evident after 4 weeks. An increase in BIC for both implant surface types occurred from weeks 2 to 4. This increase was statistically significant when compared with SLA at 2 weeks (P<0.05), but not when compared with modSLA at 2 weeks. CONCLUSION: The data from the present study demonstrate significantly more bone apposition for the modSLA surface than the standard SLA surface after 2 weeks of healing. This increased bone apposition may allow a further reduction of the healing period following implant placement for patients undergoing early loading procedures.
Authors: Thomas Ziebart; Anne Schnell; Christian Walter; Peer W Kämmerer; Andreas Pabst; Karl M Lehmann; Johanna Ziebart; Marc O Klein; Bilal Al-Nawas Journal: Clin Oral Investig Date: 2012-03-10 Impact factor: 3.573
Authors: S Lumetti; E Manfredi; S Ferraris; S Spriano; G Passeri; G Ghiacci; G Macaluso; C Galli Journal: J Mater Sci Mater Med Date: 2016-02-17 Impact factor: 3.896
Authors: Ajay Sharma; A James McQuillan; Yo Shibata; Lavanya A Sharma; John Neil Waddell; Warwick John Duncan Journal: J Mater Sci Mater Med Date: 2016-03-12 Impact factor: 3.896
Authors: Jordan Raphel; Johan Karlsson; Silvia Galli; Ann Wennerberg; Christopher Lindsay; Matthew G Haugh; Jukka Pajarinen; Stuart B Goodman; Ryo Jimbo; Martin Andersson; Sarah C Heilshorn Journal: Biomaterials Date: 2016-01-06 Impact factor: 12.479