Irini D Sideridou1, Maria M Karabela, Evagelia Ch Vouvoudi. 1. Laboratory of Organic Chemical Technology, Department of Chemistry, Aristotle University of Thessaloniki, GR-54124 Thessaloniki, Hellas, Greece. siderid@chem.auth.gr
Abstract
OBJECTIVES: The first objective of this work is the study by DMTA of viscoelastic properties (E', E'', tandelta, Tg) of two current dental resin composites Tetric EvoCeram (nanohybrid) and Heliomolar (microfilled) in dry condition and in water for up to 30 days. The second objective is to determine the sorption characteristics of these composites in water and ethanol/water solution 75vol.%. METHODS: For DMTA the bar-shaped specimens divided into five groups of three samples each. The first group consisted of dry samples measured 1h after curing. The second and third group consisted of samples, which had been heated in air at 80+/-1 degrees C for 1 day or had been stored in distilled water at 80+/-1 degrees C for 1 day. The fourth and fifth group consisted of samples, which had been stored in distilled water at 37+/-1 degrees C for periods 1 and 7 days correspondingly. Also specimen discs (15mm in diameter and 1mm in thickness) were immersed in water or a 75vol.% ethanol/water solution at 37+/-1 degrees C. At fixed time intervals they were removed, blotted dry to remove excess liquid, weighted and returned to the liquid. This process continued for 30 days. RESULTS: The viscoelastic properties (E', E'', tandelta, Tg) of the two composites treated under different conditions were recorded and compared. Also the mass uptake, diffusion coefficient, solubility and volumetric changes for immersion of composites in water and ethanol/water solution 75vol.% at 37+/-1 degrees C were determined. SIGNIFICANCE: Tetric EvoCeram a nanohybrid composite with similar about resin matrix with Heliomolar which is a microfilled showed better dynamic thermomechanical properties and sorption characteristics than Heliomolar.
OBJECTIVES: The first objective of this work is the study by DMTA of viscoelastic properties (E', E'', tandelta, Tg) of two current dental resin composites Tetric EvoCeram (nanohybrid) and Heliomolar (microfilled) in dry condition and in water for up to 30 days. The second objective is to determine the sorption characteristics of these composites in water and ethanol/water solution 75vol.%. METHODS: For DMTA the bar-shaped specimens divided into five groups of three samples each. The first group consisted of dry samples measured 1h after curing. The second and third group consisted of samples, which had been heated in air at 80+/-1 degrees C for 1 day or had been stored in distilled water at 80+/-1 degrees C for 1 day. The fourth and fifth group consisted of samples, which had been stored in distilled water at 37+/-1 degrees C for periods 1 and 7 days correspondingly. Also specimen discs (15mm in diameter and 1mm in thickness) were immersed in water or a 75vol.% ethanol/water solution at 37+/-1 degrees C. At fixed time intervals they were removed, blotted dry to remove excess liquid, weighted and returned to the liquid. This process continued for 30 days. RESULTS: The viscoelastic properties (E', E'', tandelta, Tg) of the two composites treated under different conditions were recorded and compared. Also the mass uptake, diffusion coefficient, solubility and volumetric changes for immersion of composites in water and ethanol/water solution 75vol.% at 37+/-1 degrees C were determined. SIGNIFICANCE: Tetric EvoCeram a nanohybrid composite with similar about resin matrix with Heliomolar which is a microfilled showed better dynamic thermomechanical properties and sorption characteristics than Heliomolar.