Yonca Korkmaz1, Nuray Attar. 1. Department of Conservative Dentistry, Faculty of Dentistry, Hacettepe University, Ankara, Turkey. yoncako@yahoo.com
Abstract
AIM: The purpose of this study was to investigate the effect of light-emitting diode (LED) light curing units (LCUs) compared with halogen LCUs on the shear bond strength (SBS) of one nanofill composite (Filtek Supreme) and one microhibrid composite (Artemis) with self-etch adhesives. METHODS AND MATERIALS: The buccal surfaces of 60 non-carious extracted human molars were flattened to expose dentin and, subsequently, polished for 60 seconds with 600-grit wet silicon carbide abrasive paper. Specimens were assigned into six groups (n=10) according to composite material, self-etch adhesive, and curing light used as follows: Group 1: Adper Prompt L-Pop (AP) and Filtek Supreme (FS) using an Elipar Free Light (EFL); Group 2: AP and FS using an Elipar Free Light 2 (EFL2); Group 3: AP and FS using a Hilux Expert (HE) light, Group 4: AdheSE (AS)+Artemis (AR) using an EFL; Group 5: AS+AR using an EFL2; and Group 6: AS+AR using a HE light. The specimens were thermocycled for 500 cycles (5 masculineC-55 masculineC) and then loaded to failure in a Zwick universal testing machine at a crosshead speed of 5 mm/minute. SBS values were calculated as megapascals (MPa) and statistically analyzed using the one-way analysis of variance (ANOVA) test at a significance level of 0.05. RESULTS: Mean SBS (+/- standard deviations) values were as follows: Group1: 15.99+/-5.18; Group 2: 18.76+/-6.71; Group 3: 17.70+/-5.04; Group 4: 16.93+/-3.99; Group 5: 18.01+/-5.19, and Group 6: 17.46+/-5.40. There were no statistically significant differences for SBS to dentin among the groups tested. CONCLUSION: The LED curing lights used in the study seem to be comparable with the halogen curing light for nanofill and microhybrid composites used in conjunction with self-etching systems in dentin. The EFL2 reduces curing time, which can be considered as an advantage.
AIM: The purpose of this study was to investigate the effect of light-emitting diode (LED) light curing units (LCUs) compared with halogen LCUs on the shear bond strength (SBS) of one nanofill composite (Filtek Supreme) and one microhibrid composite (Artemis) with self-etch adhesives. METHODS AND MATERIALS: The buccal surfaces of 60 non-carious extracted human molars were flattened to expose dentin and, subsequently, polished for 60 seconds with 600-grit wet silicon carbide abrasive paper. Specimens were assigned into six groups (n=10) according to composite material, self-etch adhesive, and curing light used as follows: Group 1: Adper Prompt L-Pop (AP) and Filtek Supreme (FS) using an Elipar Free Light (EFL); Group 2: AP and FS using an Elipar Free Light 2 (EFL2); Group 3: AP and FS using a Hilux Expert (HE) light, Group 4: AdheSE (AS)+Artemis (AR) using an EFL; Group 5: AS+AR using an EFL2; and Group 6: AS+AR using a HE light. The specimens were thermocycled for 500 cycles (5 masculineC-55 masculineC) and then loaded to failure in a Zwick universal testing machine at a crosshead speed of 5 mm/minute. SBS values were calculated as megapascals (MPa) and statistically analyzed using the one-way analysis of variance (ANOVA) test at a significance level of 0.05. RESULTS: Mean SBS (+/- standard deviations) values were as follows: Group1: 15.99+/-5.18; Group 2: 18.76+/-6.71; Group 3: 17.70+/-5.04; Group 4: 16.93+/-3.99; Group 5: 18.01+/-5.19, and Group 6: 17.46+/-5.40. There were no statistically significant differences for SBS to dentin among the groups tested. CONCLUSION: The LED curing lights used in the study seem to be comparable with the halogen curing light for nanofill and microhybrid composites used in conjunction with self-etching systems in dentin. The EFL2 reduces curing time, which can be considered as an advantage.