OBJECTIVE: The aim of this study was to describe the interaction pattern formed between dentin and resin on cavities prepared with an erbium laser (Er:YAG). The morphological aspect of the irradiated dentin after acid etching was also observed. METHODS: Ten dentin disks were obtained from fresh extracted third molars. Each disk received two cavities, one prepared with a conventional high-speed drill, while the other cavity was obtained by the use of an Er:YAG laser (KaVo KEY Laser, KaVo Co.). The laser treatment was performed with 250 mJ/pulse, 4Hz, non contact mode, focused beam, and a fine water mist was used. Five disks were prepared for morphological analysis of the acid etched dentin. The other five disks had their cavities restored with Single Bond (3M) followed by Z100 resin (3M). The specimens were observed under scanning electron microscopy after dentin-resin interface demineralization and deproteinization. RESULTS AND CONCLUSIONS: It was observed that the morphological characteristics of the acid-etched irradiated dentin were not favorable to the diffusion of monomers through the collagen network. The dentin-resin interfacial aspect of irradiated dentin, after acid etching, showed thin tags and scarce hybridization zones, which agreed with the morphology of the irradiated and acid-etched dentin substrate observed.
OBJECTIVE: The aim of this study was to describe the interaction pattern formed between dentin and resin on cavities prepared with an erbium laser (Er:YAG). The morphological aspect of the irradiated dentin after acid etching was also observed. METHODS: Ten dentin disks were obtained from fresh extracted third molars. Each disk received two cavities, one prepared with a conventional high-speed drill, while the other cavity was obtained by the use of an Er:YAG laser (KaVo KEY Laser, KaVo Co.). The laser treatment was performed with 250 mJ/pulse, 4Hz, non contact mode, focused beam, and a fine water mist was used. Five disks were prepared for morphological analysis of the acid etched dentin. The other five disks had their cavities restored with Single Bond (3M) followed by Z100 resin (3M). The specimens were observed under scanning electron microscopy after dentin-resin interface demineralization and deproteinization. RESULTS AND CONCLUSIONS: It was observed that the morphological characteristics of the acid-etched irradiated dentin were not favorable to the diffusion of monomers through the collagen network. The dentin-resin interfacial aspect of irradiated dentin, after acid etching, showed thin tags and scarce hybridization zones, which agreed with the morphology of the irradiated and acid-etched dentin substrate observed.
Authors: Rubens C R de Carvalho; Patricia M de Freitas; Masayuki Otsuki; Carlos P de Eduardo; Junji Tagami Journal: Lasers Med Sci Date: 2007-05-04 Impact factor: 3.161