Homayoon Alaghehmand1, Fatemeh Nezhad Nasrollah2, Hanieh Nokhbatolfoghahaei3, Reza Fekrazad4. 1. Dental Materials Researches Center, Babol Medical Sciences University, Babol, Iran. 2. Dental Material Research Center, Department of Restorative Dentistry, Faculty of Dentistry, Babol University of Medical Sciences, Babol, Iran. 3. School of Advanced Technologies in Medicine, Shahid Beheshti University of Medical Sciences, Tehran, Iran. 4. Laser Research Center in Medical Sciences (LRCMS), Department of Periodontics, Faculty of Dentistry, AJA University of Medical Sciences, Tehran, Iran ; International Network for Photo Medicine and Photo Dynamic Therapy (INPMPDT), Universal Scientific Education and Research Network (USERN), Tehran, Iran.
Abstract
Introduction: The aim of this study was to compare the micro-shear bond strength of composite resin on superficial and deep dentin after conditioning with phosphoric acid and Erbium-Doped Yttrium Aluminum Garnet (Er:YAG) laser. Methods: Thirty human molars were selected, roots were removed and crowns were bisected to provide a total of 60 half-crowns. Specimens were ground to expose superficial and deep dentin. Samples were assigned to six groups: (1) AS (acid etching of superficial dentin); (2) AD (acid etching of deep dentin); (3) LS (Er:YAG laser irradiation on superficial dentin); (4) LD (Er:YAG laser irradiation on deep dentin); (5) LAS (Er:YAG laser irradiation on superficial dentin followed by acid etching); (6) LAD (Er:YAG laser irradiation on deep dentin followed by acid etching) The adhesive protocol was performed. Samples were thermocycled and micro-shear bond strength was tested to failure. The data were submitted to statistical analysis with one-way analysis of variance (ANOVA) and Tukey post hoc test. Results: The AS group, demonstrated the greatest amount of micro-shear bond strength. Statistical analysis showed a decrease in bond strength in laser-treated groups which was more significant for deep dentin. Conclusion: Preparation of dentin with laser did not improve bonding to superficial and deep dentin.
Introduction: The aim of this study was to compare the micro-shear bond strength of composite resin on superficial and deep dentin after conditioning with phosphoric acid and Erbium-Doped Yttrium Aluminum Garnet (Er:YAG) laser. Methods: Thirty human molars were selected, roots were removed and crowns were bisected to provide a total of 60 half-crowns. Specimens were ground to expose superficial and deep dentin. Samples were assigned to six groups: (1) AS (acid etching of superficial dentin); (2) AD (acid etching of deep dentin); (3) LS (Er:YAG laser irradiation on superficial dentin); (4) LD (Er:YAG laser irradiation on deep dentin); (5) LAS (Er:YAG laser irradiation on superficial dentin followed by acid etching); (6) LAD (Er:YAG laser irradiation on deep dentin followed by acid etching) The adhesive protocol was performed. Samples were thermocycled and micro-shear bond strength was tested to failure. The data were submitted to statistical analysis with one-way analysis of variance (ANOVA) and Tukey post hoc test. Results: The AS group, demonstrated the greatest amount of micro-shear bond strength. Statistical analysis showed a decrease in bond strength in laser-treated groups which was more significant for deep dentin. Conclusion: Preparation of dentin with laser did not improve bonding to superficial and deep dentin.
Entities:
Keywords:
acid-etch; bond strength; composite; laser; micro-shear bond strength