OBJECTIVES: The aim of this in vitro study was to evaluate the color stability of modern light-cured composites when subjected to various physico-chemical and staining conditions. METHODS: Ten brands were evaluated including hybrids, microfine hybrids and microfilled composites. Some universal shade samples underwent only staining tests, while others were subjected to one of the following experimental conditions: thermocycling, postcuring, polishing or a 1 wk immersion in saline, prior to staining. The coloring solutions used for the staining tests were: coffee, E 110 food dye, vinegar and erythrosin. A colorimetric evaluation according to the CIE L*a*b* system was performed after experimental periods of 1 and 3 wk. RESULTS: Erythrosin caused the greatest color change for the composites tested. A reduced susceptibility to staining was observed where surfaces had been polished. Low water sorption, a high filler-resin ratio, reduced particle size and hardness, and an optimal filler-matrix coupling system were related to improved composite resistance to discoloration. SIGNIFICANCE: Resistance of modern composites to discolorations still depends on their structure and manipulation.
OBJECTIVES: The aim of this in vitro study was to evaluate the color stability of modern light-cured composites when subjected to various physico-chemical and staining conditions. METHODS: Ten brands were evaluated including hybrids, microfine hybrids and microfilled composites. Some universal shade samples underwent only staining tests, while others were subjected to one of the following experimental conditions: thermocycling, postcuring, polishing or a 1 wk immersion in saline, prior to staining. The coloring solutions used for the staining tests were: coffee, E 110 food dye, vinegar and erythrosin. A colorimetric evaluation according to the CIE L*a*b* system was performed after experimental periods of 1 and 3 wk. RESULTS:Erythrosin caused the greatest color change for the composites tested. A reduced susceptibility to staining was observed where surfaces had been polished. Low water sorption, a high filler-resin ratio, reduced particle size and hardness, and an optimal filler-matrix coupling system were related to improved composite resistance to discoloration. SIGNIFICANCE: Resistance of modern composites to discolorations still depends on their structure and manipulation.