Triazine Compound as Copolymerized Antibacterial Agent in Adhesive Resins.

The aim of this study was to formulate and evaluate an experimental adhesive resin with the addition of 1,3,5-triacryloylhexahydro-1,3,5-triazine at different concentrations. Experimental adhesive resins were obtained by mixing 50% wt bisphenol A glycol dimethacrylate (BisGMA), 25% wt triethylene glycol dimethacrylate (TEGDMA), 25% wt 2-hydroxyethyl methacrylate (HEMA) and photoinitiator system. The triazine compound was added in 1, 2.5 and 5% wt to a base adhesive resin and one group remained with no triazine as control group. The experimental adhesive resins were analyzed for antibacterial activity (n=3), degree of conversion (n=3) and softening in solvent (n=3). Data distribution was evaluated by Kolmogorov-Smirnov test, paired t test, one-way ANOVA and Tukey's with a 0.05 level of significance. All groups with added triazine compound showed antibacterial activity against Streptococcus mutans (p<0.05). All groups achieved more than 70% degree of conversion, but there was no difference in this chemical property (p>0.05). The initial Knoop hardness was higher in 2.5 and 5% wt groups (p<0.05) and both groups present lower percentage variation of Knoop hardness after solvent degradation. The present study formulated an antibacterial adhesive resin with a non-releasing agent able to copolymerize with the comonomeric blend, improving the restorative material's properties.