Amandeep Dosanjh1, Susan Paurazas2, Mazin Askar2. 1. Department of Postgraduate Endodontics, University of Detroit Mercy, Detroit, Michigan. Electronic address: andydosanjh@gmail.com. 2. Department of Postgraduate Endodontics, University of Detroit Mercy, Detroit, Michigan.
Abstract
INTRODUCTION: This study examined the effect of different temperatures on the cyclic fatigue of nickel-titanium rotary files. METHODS: Three groups of nickel-titanium rotary files (EF group [EdgeFile; EdgeEndo, Albuquerque, NM], VB group [Vortex Blue; Dentsply Tulsa Dental Specialties, Tulsa, OK], and ESX group [ESX; Brasseler USA, Savannah, GA]) of size 25 with a .04 taper and 25-mm length were tested in a metal block that simulated a canal curvature of 60° and a 5-mm radius curvature. The block was submerged in a water bath filled with water at 3°C, 22°C, 37°C, and 60°C. At each temperature, 30 files from each group were rotated at 500 rpm in the block. The number of cycles to fracture (NCF) was calculated. Statistical analysis was completed using a 1-way analysis of variance with significance at P < .05. RESULTS: VB group showed a significant decrease in NCF as the temperature increased from 3°C to 60°C. The ESX group showed a significant decrease in NCF as the temperature increased from 3°C to 37°C. The EF group showed a significant increase in NCF from 3°C to 22°C and a significant decrease in NCF from 22°C to 37°C. For each temperature, the EF group showed higher NCF than the VB group, which showed higher NCF than the ESX group. CONCLUSIONS: In this in vitro study, temperature was found to significantly affect the cyclic fatigue of nickel-titanium rotary files. At each tested temperature, NCF was the highest for the EF group followed by the VB group and lowest for the ESX group. Future cyclic fatigue studies should be conducted at body temperature.
INTRODUCTION: This study examined the effect of different temperatures on the cyclic fatigue of nickel-titanium rotary files. METHODS: Three groups of nickel-titanium rotary files (EF group [EdgeFile; EdgeEndo, Albuquerque, NM], VB group [Vortex Blue; Dentsply Tulsa Dental Specialties, Tulsa, OK], and ESX group [ESX; Brasseler USA, Savannah, GA]) of size 25 with a .04 taper and 25-mm length were tested in a metal block that simulated a canal curvature of 60° and a 5-mm radius curvature. The block was submerged in a water bath filled with water at 3°C, 22°C, 37°C, and 60°C. At each temperature, 30 files from each group were rotated at 500 rpm in the block. The number of cycles to fracture (NCF) was calculated. Statistical analysis was completed using a 1-way analysis of variance with significance at P < .05. RESULTS: VB group showed a significant decrease in NCF as the temperature increased from 3°C to 60°C. The ESX group showed a significant decrease in NCF as the temperature increased from 3°C to 37°C. The EF group showed a significant increase in NCF from 3°C to 22°C and a significant decrease in NCF from 22°C to 37°C. For each temperature, the EF group showed higher NCF than the VB group, which showed higher NCF than the ESX group. CONCLUSIONS: In this in vitro study, temperature was found to significantly affect the cyclic fatigue of nickel-titanium rotary files. At each tested temperature, NCF was the highest for the EF group followed by the VB group and lowest for the ESX group. Future cyclic fatigue studies should be conducted at body temperature.
Authors: Jorge N R Martins; Duarte Marques; Isabel Vasconcelos; Sofia Arantes-Oliveira; João Caramês; Francisco Manuel Braz Fernandes Journal: Dent J (Basel) Date: 2022-02-17
Authors: Javier Nino-Barrera; Jose Sanchez-Aleman; Manuel Acosta-Humanez; Luis Gamboa-Martinez; Carlos Cortes-Rodriguez Journal: Sci Rep Date: 2021-06-21 Impact factor: 4.379