J A Duque1, S L Fernandes1, J P Bubola1, M A H Duarte1, J Camilleri2, M A Marciano3. 1. Department of Dentistry, Dental School of Bauru, University of São Paulo (USP), Bauru, SP, Brazil. 2. Department of Restorative Dentistry, Faculty of Dental Surgery, University of Malta, Msida, Malta. 3. Piracicaba Dental School, State University of Campinas, Piracicaba, SP, Brazil.
Abstract
AIM: To evaluate the effect of three methods of mixing on the physical and chemical properties of tricalcium silicate-based cements. METHODOLOGY: The materials evaluated were MTA Angelus and Portland cement with 20% zirconium oxide (PC-20-Zr). The cements were mixed using a 3 : 1 powder-to-liquid ratio. The mixing methods were manual (m), trituration (tr) and ultrasonic (us) activation. The materials were characterized by means of scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy. Flowability was analysed according to ANSI/ADA 57/2012. Initial and final setting times were assessed following ASTM C266/08. Volume change was evaluated using a micro-CT volumetric method. Solubility was analysed according to ADA 57/2012. pH and calcium ion release were measured after 3, 24, 72 and 168 h. Statistical analysis was performed using two-way analysis of variance. The level of significance was set at P = 0.05. RESULTS: The SEM analysis revealed that ultrasonic activation was associated with a homogeneous distribution of particles. Flowability, volume change and initial setting time were not influenced by the mixing method (P > 0.05). Solubility was influenced by the mixing method (P < 0.05). For pH, at 168 h, significant differences were found between MTA-m and PC-20-Zr-m (P < 0.05). For calcium ion release, PC-20-Zr-tr had higher values than MTA-m at 3 h, and MTA-tr had higher values than PC-20-Zr-m at 168 h (P < 0.05). CONCLUSIONS: The ultrasonic and trituration methods led to higher calcium ion release and pH compared with manual mixing for all cements, whilst the ultrasonic method produced smaller particles for the PC-20-Zr cement. Flow, setting times and volume change were not influenced by the mixing method used; however, it did have an impact on solubility.
AIM: To evaluate the effect of three methods of mixing on the physical and chemical properties of tricalcium silicate-based cements. METHODOLOGY: The materials evaluated were MTA Angelus and Portland cement with 20% zirconium oxide (PC-20-Zr). The cements were mixed using a 3 : 1 powder-to-liquid ratio. The mixing methods were manual (m), trituration (tr) and ultrasonic (us) activation. The materials were characterized by means of scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy. Flowability was analysed according to ANSI/ADA 57/2012. Initial and final setting times were assessed following ASTM C266/08. Volume change was evaluated using a micro-CT volumetric method. Solubility was analysed according to ADA 57/2012. pH and calcium ion release were measured after 3, 24, 72 and 168 h. Statistical analysis was performed using two-way analysis of variance. The level of significance was set at P = 0.05. RESULTS: The SEM analysis revealed that ultrasonic activation was associated with a homogeneous distribution of particles. Flowability, volume change and initial setting time were not influenced by the mixing method (P > 0.05). Solubility was influenced by the mixing method (P < 0.05). For pH, at 168 h, significant differences were found between MTA-m and PC-20-Zr-m (P < 0.05). For calcium ion release, PC-20-Zr-tr had higher values than MTA-m at 3 h, and MTA-tr had higher values than PC-20-Zr-m at 168 h (P < 0.05). CONCLUSIONS: The ultrasonic and trituration methods led to higher calcium ion release and pH compared with manual mixing for all cements, whilst the ultrasonic method produced smaller particles for the PC-20-Zr cement. Flow, setting times and volume change were not influenced by the mixing method used; however, it did have an impact on solubility.
Authors: Lauter E Pelepenko; Flavia Saavedra; Thiago B M Antunes; Gabriela F Bombarda; Brenda P F A Gomes; Alexandre A Zaia; Josette Camilleri; Marina A Marciano Journal: Clin Oral Investig Date: 2020-08-31 Impact factor: 3.573
Authors: Fredson Márcio Acris De Carvalho; Yara Teresinha Corrêa Silva-Sousa; Carlos Eduardo Saraiva Miranda; Paulo Henrique Miller Calderon; Ana Flávia Simões Barbosa; Luciana Martins Domingues De Macedo; Fuad Jacob Abi Rached-Junior Journal: Int J Dent Date: 2021-01-27