A facile and green strategy for the synthesis of Au, Ag and Au-Ag alloy nanoparticles using aerial parts of R. hypocrateriformis extract and their biological evaluation.

A facile and green strategy is reported here to synthesize gold (Au), silver (Ag) and gold-silver (Au-Ag) alloy nanoparticles (NPs) through bio-reduction reactions of aqueous corresponding metal precursors mediated by extracts of aerial parts of R. hypocrateriformis, which act as both reducing and stabilizing agents, under microwave irradiation. UV-vis spectrophotometer, XRD, FT-IR, FESEM/TEM, TGA and EDAX analysis were used to characterize the obtained NPs. The formation of NPs is evident from their surface plasmon resonance peak observed at λmax=∼550, 450 and 500nm for Au, Ag and Au-Ag alloy NPs respectively. XRD pattern revealed that fcc structure, while FT-IR spectra signify the presence of phytochemicals adsorbed on NPs. Such a biofunctionalized NPs were characterized by their weight loss, 30% due to thermal degradation of plant phytochemicals observed in TG analysis. The spherical shape of Au, Ag and Au-Ag alloy NPs (∼10-50nm) is observed by FE-SEM/TEM images. EDAX analysis confirms the expected elemental composition. Moreover, these NPs showed enhanced antimicrobial, antioxidant, and anticancer activities, though it is more pronounced for Au-Ag alloy NPs, which is due to the combining effect of phytochemicals, Au and Ag metals. Thus, the biosynthesized NPs could be applied as effective growth inhibitors for various biomedical applications.