Daniel S Thoma1, Ui-Won Jung2, Jin-Young Park2, Stefan P Bienz1, Jürg Hüsler1, Ronald E Jung1. 1. Clinic of Fixed and Removable Prosthodontics and Dental Material Science, University of Zurich, Zurich, Switzerland. 2. Department of Periodontology, Research Institute for Periodontal Regeneration, College of Dentistry, Yonsei University, Seoul, South Korea.
Abstract
OBJECTIVES: The aim of the study was to test whether or not the use of a polyethylene glycol (PEG) hydrogel with or without the addition of an arginylglycylaspartic acid (RGD) sequence applied as a matrix in combination with hydroxyapatite/tricalciumphosphate (HA/TCP) results in similar peri-implant bone regeneration as traditional guided bone regeneration procedures. MATERIAL AND METHODS: In 12 beagle dogs, implant placement and peri-implant bone regeneration were performed 2 months after tooth extraction in the maxilla. Two standardized box-shaped defects were bilaterally created, and dental implants were placed in the center of the defects with a dehiscence of 4 mm. Four treatment modalities were randomly applied: i)HA/TCP mixed with a synthetic PEG hydrogel, ii)HA/TCP mixed with a synthetic PEG hydrogel supplemented with an RGD sequence, iii)HA/TCP covered with a native collagen membrane (CM), iv)and no bone augmentation (empty). After a healing period of 8 or 16 weeks, micro-CT and histological analyses were performed. RESULTS: Histomorphometric analysis revealed a greater relative augmented area for groups with bone augmentation (43.3%-53.9% at 8 weeks, 31.2%-42.8% at 16 weeks) compared to empty controls (22.9% at 8 weeks, 1.1% at 16 weeks). The median amount of newly formed bone was greatest in group CM at both time-points. Regarding the first bone-to-implant contact, CM was statistically significantly superior to all other groups at 8 weeks. CONCLUSIONS: Bone can partially be regenerated at peri-implant buccal dehiscence defects using traditional guided bone regeneration techniques. The use of a PEG hydrogel applied as a matrix mixed with a synthetic bone substitute material might lack a sufficient stability over time for this kind of defect.
OBJECTIVES: The aim of the study was to test whether or not the use of a polyethylene glycol (PEG) hydrogel with or without the addition of an arginylglycylaspartic acid (RGD) sequence applied as a matrix in combination with hydroxyapatite/tricalciumphosphate (HA/TCP) results in similar peri-implant bone regeneration as traditional guided bone regeneration procedures. MATERIAL AND METHODS: In 12 beagle dogs, implant placement and peri-implant bone regeneration were performed 2 months after tooth extraction in the maxilla. Two standardized box-shaped defects were bilaterally created, and dental implants were placed in the center of the defects with a dehiscence of 4 mm. Four treatment modalities were randomly applied: i)HA/TCP mixed with a synthetic PEG hydrogel, ii)HA/TCP mixed with a synthetic PEG hydrogel supplemented with an RGD sequence, iii)HA/TCP covered with a native collagen membrane (CM), iv)and no bone augmentation (empty). After a healing period of 8 or 16 weeks, micro-CT and histological analyses were performed. RESULTS: Histomorphometric analysis revealed a greater relative augmented area for groups with bone augmentation (43.3%-53.9% at 8 weeks, 31.2%-42.8% at 16 weeks) compared to empty controls (22.9% at 8 weeks, 1.1% at 16 weeks). The median amount of newly formed bone was greatest in group CM at both time-points. Regarding the first bone-to-implant contact, CM was statistically significantly superior to all other groups at 8 weeks. CONCLUSIONS: Bone can partially be regenerated at peri-implant buccal dehiscence defects using traditional guided bone regeneration techniques. The use of a PEG hydrogel applied as a matrix mixed with a synthetic bone substitute material might lack a sufficient stability over time for this kind of defect.
Authors: Siwen Wang; Weiyi Wu; Yuhua Liu; Xinzhi Wang; Lin Tang; Pengyue You; Jianmin Han; Bowen Li; Yi Zhang; Mei Wang Journal: Biomed Res Int Date: 2019-11-16 Impact factor: 3.411
Authors: Talia Cohen; Olga Kossover; Eli Peled; Tova Bick; Lena Hasanov; Tan Tuan Chun; Simon Cool; Dina Lewinson; Dror Seliktar Journal: J Tissue Eng Regen Med Date: 2022-02-04 Impact factor: 4.323