R N Akash1, Satyabodh S Guttal2. 1. Private Practice, Pune, India. 2. Department of Prosthodontics, SDM College of Dental Sciences & Hospital, Dharwad, Karnataka, India.
Abstract
PURPOSE: The aim of this study was to evaluate the effect of incorporation of two compositions of nano-oxides on color stability of intrinsically colored maxillofacial silicone elastomer subjected to outdoor weathering. MATERIALS AND METHODS: Ninety Cosmesil M511 silicone elastomer specimens were fabricated. The control group was incorporated with intrinsic coloring agents (umber, brown, yellow), group A was incorporated with intrinsic coloring agents and nanosized titanium oxide (TiO2 ), and group B was incorporated with intrinsic coloring agents and nanosized zinc oxide (ZnO). For outdoor weathering, specimens were mounted on a treated plywood rack, and the assembly was weathered for 6 months. A GretagMacbeth Spectrolino spectrophotometer was used to determine the CIELAB (L*a*b*) parameter before and after weathering of each specimen, and the values were noted. The color change (∆E) values were analyzed by one-way ANOVA, Tukey's post hoc test, and paired t-test. RESULTS: The color change (ΔE*) for groups were control group > group A > group B. The control group (0.76 ± 0.32) and group A (0.47 ± 0.19) showed significant difference in the color change before and after weathering (p < 0.00001). Group B (0.03 ± 0.05) showed no significant difference in color change before and after weathering (p = 0.08). CONCLUSIONS: The present findings suggest that incorporation of nano-oxides improved the color stability of Cosmesil M511 silicone elastomer and also acted as an opacifier. ZnO-incorporated Cosmesil M511 specimens showed minimal or no color change and proved to be most color stable after being subjected to outdoor weathering.
PURPOSE: The aim of this study was to evaluate the effect of incorporation of two compositions of nano-oxides on color stability of intrinsically colored maxillofacial silicone elastomer subjected to outdoor weathering. MATERIALS AND METHODS: Ninety Cosmesil M511 silicone elastomer specimens were fabricated. The control group was incorporated with intrinsic coloring agents (umber, brown, yellow), group A was incorporated with intrinsic coloring agents and nanosized titanium oxide (TiO2 ), and group B was incorporated with intrinsic coloring agents and nanosized zinc oxide (ZnO). For outdoor weathering, specimens were mounted on a treated plywood rack, and the assembly was weathered for 6 months. A GretagMacbeth Spectrolino spectrophotometer was used to determine the CIELAB (L*a*b*) parameter before and after weathering of each specimen, and the values were noted. The color change (∆E) values were analyzed by one-way ANOVA, Tukey's post hoc test, and paired t-test. RESULTS: The color change (ΔE*) for groups were control group > group A > group B. The control group (0.76 ± 0.32) and group A (0.47 ± 0.19) showed significant difference in the color change before and after weathering (p < 0.00001). Group B (0.03 ± 0.05) showed no significant difference in color change before and after weathering (p = 0.08). CONCLUSIONS: The present findings suggest that incorporation of nano-oxides improved the color stability of Cosmesil M511 silicone elastomer and also acted as an opacifier. ZnO-incorporated Cosmesil M511 specimens showed minimal or no color change and proved to be most color stable after being subjected to outdoor weathering.