E Pedullà1, F Lo Savio2, S Boninelli3, G Plotino4, N M Grande4, E Rapisarda1, G La Rosa2. 1. Department of Surgery, University of Catania, Catania, Italy. 2. Department of Industrial Engineering, University of Catania, Catania, Italy. 3. MATIS, Institute of Microelectronics and Microsystems, National Research Council, Catania, Italy. 4. Department of Endodontics, 'Sapienza' University of Rome, Rome, Italy.
Abstract
AIM: To evaluate the effect of different torsional preloads on cyclic fatigue resistance of endodontic rotary instruments constructed from conventional nickel-titanium (NiTi), M-Wire or CM-Wire. METHODOLOGY: Eighty new size 25, 0.06 taper Mtwo instruments (Sweden & Martina), size 25, 0.06 taper HyFlex CM (Coltene/Whaledent, Inc) and X2 ProTaper Next (Dentsply Maillefer) were used. The Torque and distortion angles at failure of new instruments (n = 10) were measured, and 0% (n = 10), 25%, 50% and 75% (n = 20) of the mean ultimate torsional strength as preloading condition were applied according to ISO 3630-1 for each brand. The twenty files tested for every extent of preload were subjected to 20 or 40 torsional cycles (n = 10). After torsional preloading, the number of cycles to failure was evaluated in a simulated canal with 60° angle of curvature and 5 mm of radius of curvature. Data were analysed using two-way analysis of variance. The fracture surface of each fragment was examined with a scanning electron microscope (SEM). Data were analysed by two-way analyses of variance. RESULTS: Preload repetitions did not influence the cyclic fatigue of the three brands; however, the 25%, 50% and 75% torsional preloading significantly reduced the fatigue resistance of all instruments tested (P < 0.01, P < 0.001 and P < 0.0001, respectively) except for the HyFlex CM preloaded with 25% of the maximum torsional strength (P > 0.05). CONCLUSIONS: Torsional preloads reduced the cyclic fatigue resistance of conventional and treated (M-wire and CM-wire) NiTi rotary instruments except for size 25, 0.06 taper HyFlex CM instruments with a 25% of torsional preloading.
AIM: To evaluate the effect of different torsional preloads on cyclic fatigue resistance of endodontic rotary instruments constructed from conventional nickel-titanium (NiTi), M-Wire or CM-Wire. METHODOLOGY: Eighty new size 25, 0.06 taper Mtwo instruments (Sweden & Martina), size 25, 0.06 taper HyFlex CM (Coltene/Whaledent, Inc) and X2 ProTaper Next (Dentsply Maillefer) were used. The Torque and distortion angles at failure of new instruments (n = 10) were measured, and 0% (n = 10), 25%, 50% and 75% (n = 20) of the mean ultimate torsional strength as preloading condition were applied according to ISO 3630-1 for each brand. The twenty files tested for every extent of preload were subjected to 20 or 40 torsional cycles (n = 10). After torsional preloading, the number of cycles to failure was evaluated in a simulated canal with 60° angle of curvature and 5 mm of radius of curvature. Data were analysed using two-way analysis of variance. The fracture surface of each fragment was examined with a scanning electron microscope (SEM). Data were analysed by two-way analyses of variance. RESULTS: Preload repetitions did not influence the cyclic fatigue of the three brands; however, the 25%, 50% and 75% torsional preloading significantly reduced the fatigue resistance of all instruments tested (P < 0.01, P < 0.001 and P < 0.0001, respectively) except for the HyFlex CM preloaded with 25% of the maximum torsional strength (P > 0.05). CONCLUSIONS: Torsional preloads reduced the cyclic fatigue resistance of conventional and treated (M-wire and CM-wire) NiTi rotary instruments except for size 25, 0.06 taper HyFlex CM instruments with a 25% of torsional preloading.
Authors: Giuseppe Troiano; Mario Dioguardi; Armando Cocco; Giovanni Giannatempo; Luigi Laino; Domenico Ciavarella; Elio Berutti; Lorenzo Lo Muzio Journal: Open Dent J Date: 2016-10-07
Authors: Giuseppe Troiano; Mario Dioguardi; Armando Cocco; Michele Giuliani; Cristiano Fabiani; Alfonso D'Alessandro; Domenico Ciavarella; Lorenzo Lo Muzio Journal: ScientificWorldJournal Date: 2016-12-08
Authors: Sílvio Emanuel Acioly Conrado de Menezes; Shirley Machado Batista; Diego Felipe Brandão de Magalhães; de Albuquerque Diana Santana; Gabriela Queiroz de Melo Monteiro Journal: Iran Endod J Date: 2018