First-principles study on the phase diagram and multiferroic properties of (SrCoO3)1/(SrTiO3)1 superlattices.

To design a multiferroic material at atomic scale, strong spin-lattice and charge-lattice couplings play crucial roles. Our first-principles calculation on (SrCoO3)1/(SrTiO3)1 superlattices, with above coupling properties, yields a rich physical phase diagram as a function of epitaxial strain. In particular, a robust ferroelectric ferromagnetic insulator of Pc symmetry is stabilized at tensile strain Δa/a0 = 0.86%-5.53%. The polarization can be as large as 36 μC/cm(2) and magnetic moment can reach 6 μB per unit cell. The magnetocrystalline anisotropy energy (0.16 meV/Co in (001) plane, 0.6 meV/Co in (100) plane) is comparable with that of TbMnO3 compound and the magnetoelectric constant α (1.44 × 10(-3) Gaussian unit) is comparable with that of Co3B7O13Br compound. Our study suggests that epitaxially strained (SrCoO3)1/(SrTiO3)1 superlattices not only offer an excellent candidate for multiferroic materials, but also demonstrate the half-metal and ferromagnetic insulator properties with potential application in spintronic devices.

A ferroelectric ferromagnetic insulator can be a good candidate for multiferroic materials if the cross control of polarization or magnetization by magnetic or electric field can be manipulated12. Thus, a satisfactory multiferroic compound not only possesses large polarization and magnetization, but also requires strong magnetoelectric coupling34. As device miniaturization demands integrating electronic and magnetic components together, searching for new multiferroic materials constitutes an important research direction56.

The perovskite family of compounds offers an excellent candidate for multiferroic materials because of the strong coupling among spin, charge, and orbital degrees of freedom78. In particular, the subtle balance between different competing interactions makes the structural tuning very effective so that novel phenomena appear in the presence of either compressive or tensile strain91011. Among others, Lee et al. demonstrated the feasibility of converting nonferroelectric and nonferromagnetic EuTiO3 films into multiferroics under epitaxial tensile strain imposed by substrates1213. The critical temperature T ( = 4.24 K) was very low, it, nevertheless, provided a new direction to explore multiferroic materials. The substrate induced strain also helps to make the LuFeO3 thin films a room temperature multiferroic, a weak ferromagnetism was observed at 130 K resulting from spin reorientation phenomena14. Inspired by the experimental advances, the first-principles studies have also offered valuable information in this endeavor. The multiferroic property has been predicted by Lee et al. in SrMnO3 thin films under epitaxial strain and T = 92 K was estimated15. An interesting phase transition between a ferromagnetic metal and ferroelectric antiferromagnetic (AFM) insulator is also shown in strained SrCoO3 thin film16. There are also attempts to transform ferroelectric compounds into multiferroic compounds by doping. For instance, ferromagnetism was induced in V-doped ferroelectric La2Ti2O7 compound17, but the magnetoelectric coupling was too weak to function as a multiferroic. Although great processes have been made in the search of multiferroic materials, many important issues remain unresolved. The critical temperature is still low which hinders applications; compounds with both large polarization and magnetization are rare; even if large polarization and magnetization have been achieved, strong magnetoelectric coupling still needs to be dealt with.

Since epitaxial strain plays such an important role in tuning material properties, combining crystals with similar structures but complementary properties into superlattices can be a good option1819. One expects that the resultant materials might combine the characteristics of their constituents. Furthermore, interface mediated strain effectively couples the physical properties of their constituents so that the cross controls of constituent properties can be realized. In the recent studies on superlattice structures, the improper ferroelectric effect was found in PbTiO3/SrTiO3 superlattices18 and a large magnetoelectric coupling was also observed in nonferroelectric NdMnO3/SrMnO3/LaMnO3 superlattices19. To shed further insight of interface effect on material properties, we have studied, in this Report, the electronic and magnetic properties of (SrCoO3)1/(SrTiO3)1 superlattice (made of SrCoO3 and SrTiO3 layers of one cubic-cell thick, SCO/STO). As is well known, SrCoO3 is a prototype spin-state transition compound20 and possesses strong Jahn-Teller effect while SrTiO311, though belongs to paraelectric compound, is near the ferroelectric instability. It is hoped that large ferroelectricity and ferromagnetism can arise from its constituent compounds while strong magnetoelectric coupling can be achieved by the interface mediated spin-lattice and charge-lattice couplings.

To explore the phase diagram of SCO/STO superlattices, possible crystal structures with different oxygen octahedra tilting (OOT) patterns are derived from the unstable phonon modes of high symmetry P4/mmm structure and their relative stabilities are analyzed. In Glazer's notation21, the considered metastable crystal structures include: P4/mmm (a0a0c0), P4mm (), Amm2 (), P4/mbm (a0a0c+), C2/m (a−a0c0), Pmna (a−a−c0), P21/c (a−a−c+), Pbam (P4/mbm with Jahn-Teller distortion), P4bm (P4/mbm + ), Cm (C2/m + ), Pma2 (Pmna + ), Pc (P21/c + ), and Pba2(Pbam + ) symmetries. and refer to the polar distortion modes perpendicular and parallel to the (001) plane of superlattices (see Supplementary Information). In addition, both ferromagnetic (FM) and nearest neighbor antiferromagnetic (AFM) states are considered for cobalt moments. Although the Co-ion is well known for its varying spin-state depending on crystal field, the intermediate spin-state turns out to be the convergent solution in the whole epitaxial strain range we studied. In our numerical calculations, for a given initial structure with characteristic OOT pattern and polar distortion, we search for the convergent metastable solution driven by the structural and atomic relaxations. The convergent solution can be either the one with the same symmetry as the initial trial solution or a solution with different symmetry.

Results

In Fig. 1, we plot the energies of those possible ground states for the strain range e = −5.6% ~ 5.89%. As strain varies from compression to tensile, the ground state of the superlattices changes consecutively from the antiferromagnetic metal of P4mm symmetry to the ferromagnetic half-metal, insulator, and again half-metal of Pbam symmetry, then to the ferromagnetic insulators with almost degenerate P21/c and C2/m symmetries, and is followed by the robust multiferroic insulator of Pc symmetry with large polarization and magnetization combined with strong magnetoelectric coupling. This state is finally replaced by the antiferromagnetic insulator of Pc structure. To correlate the electromagnetic properties of possible ground states with the specific crystal structures, the lattice constant c, OOT, band-gap, and exchange energy are presented in Fig. 2. AAFD of Fig. 2b stands for the anti-phase antiferro-distortive vector of OOT22, its three components are the tilting angles along the pseudo-cubic crystal cell ([100], [010], and [001]). Since the AAFD vectors for CoO6 and TiO6 octahedra are complementary to each other, only AAFD vectors for CoO6 octahedra are shown.

Figure 1

Energies of SCO/STO superlattices as functions of epitaxial strain e for the various possible ground states of different symmetries.

e = (a − a0)/a0 is defined with respect to the equilibrium lattice constant a0 = 3.940Å of SrTiO3. The vertical lines mark the phase boundaries between different symmetries while the dotted vertical line represents the metal-insulator boundary within the same structural symmetry.

Figure 2

Structural and electronic properties of SCO/STO superlattices versus epitaxial strain for the various possible ground states.

(a) Lattice constant c; (b) AAFD vector. Dashed, dotted, and solid lines represent x, y, z components, respectively; (c) Band gaps. Solid and dotted lines refer to spin-up and spin-down bands; (d) Exchange energy ΔE = E − E.

Below we discuss the electronic and magnetic properties of various possible ground states one by one. For −5.6% < e ≤ −4.3%, the most stable state is an AFM metal with P4mm symmetry (see Supplementary Information). This state has no OOT and the band gaps for both spin-up and spin-down bands are zero. The projected electron occupation number and magnetic moment on Co-d orbitals are and . The Co ions take an intermediate-spin state and form an AFM order.

As strain e approaches −4.3%, above AFM state is replaced by a ferromagnetic state with Pbam symmetry. From the band-gap shown in Fig. 2c, this state is initially a half metal with perfect spin polarization. The half-metal state is further developed into a ferromagnetic insulator at e = −3.45%. The band-gaps for both spin-up and spin-down bands become nonzero though one decreases while another increases with epitaxial strain e. A half-metal state with reversed spin polarization could be recovered at e = −0.01% which is, however, beyond the border (e = −0.57%) of stability for this state. AAFD vector changes very slowly with epitaxial strain, the only nonzero titling angle along z-axis changes from 1.38° to 1.02° in the strain range (−4.3%, −0.57%). The electron occupation number () is almost unchanged while magnetic moment () is reduced. These half-metal and ferromagnetic insulator may find their applications in spintronic devices23.

In the region −0.57% < e ≤ 0.86% where strain is small, the two ferromagnetic insulators with separate P21/c and C2/m symmetries appear as the most stable states. These two states are almost degenerate in energy and their crystal structures are all of monoclinic crystal class. Similar case was also found previously in EuTiO324. The lattice constants and exchange energies have similar values. The electron occupation numbers and magnetic moments are almost identical, for both states. The band-gaps for spin-up bands are of the same sizes while the band-gaps for spin-down differ by a factor of two. This is caused by the different crystal structures. For P21/c structure, AAFD vector changes from (2.90°, 3.10°, 0.02°) to (3.68°, 3.89°, 0°). The x and y components are quite close, though not identical due to the orbital ordering similar to that in LaMnO323. For C2/m structure, only x component of AAFD vector is nonzero and takes the value 4.17° ~ 5.39° in the corresponding strain range.

At tensile strain e = 0.86%, both energies and first derivatives of energies with respect to strain e are identical for P21/c and Pc structures. Thus, a second order phase transition takes place from P21/c to Pc structure. These two states are quite similar magnetically except the polar distortion in Pc structure. The ferromagnetic insulator is still kept in Pc structure and the band-gaps evolve continuously upwards with e. In the strain range (0.86%, 5.53%) stable for Pc structure, the AAFD vector varies from (3.68°, 3.89°, 0.00°) to (9.23°, 3.23°, 0.39°). The electron occupation number and magnetic moment are almost the same as those of P21/c structure. The total magnetic moment is 6μ. The most striking feature of this state is the large polarization as shown in Fig. 3. The calculated polarization with respect to P21/c reference structure lies along [uuv] direction with u≠v. It increases linearly from (0, 0, 0) to (−23.9 μC/cm2, −23.9 μC/cm2, 12.75 μC/cm2) with the inclination angle of about 27°. This robust multiferroic state is a proper multiferroic state similar to the Pmc21 state found by Lee et al.15. It differs from the multiferroic states studied by other groups where only weak ferromagnetism or antiferromagnetism is found to coexist with ferroelectric order142526.

Figure 3

The polarization of the robust multiferroic state of Pc structure as a function of tensile strain.

Further increasing the tensile strain destabilizes the ferromagnetic state and the AFM insulator of Pc structure becomes stable for e > 5.53%. The x and y components of the AAFD vector are reduced significantly while the z component increases considerably. In comparison with the FM state of Pc structure, this state has the similar electron occupation number () and slightly reduced magnetic moment (). This state is also a multiferroic state, the calculated polarization is (27.9 μC/cm2, 34.0 μC/cm2, 32.9 μC/cm2) at e = 5.89%.

To shed further insight into the physical properties of the multiferroic state of Pc structure, the spin and orbital resolved partial densities of states (PDOS) are presented in Fig. 4. The epitaxial strain is set at e = 2.3% and Fermi energy is set as zero. The Co-d orbitals are decomposed into triplet t2(d, d, d) and doublet sets with respect to CoO6 octahedron. The two nearest neighbors Co-I and Co-II ions are included in order to illustrate charge and orbital ordering phenomena. It is seen that the multiferroic state is an insulator with a band-gap of 0.12 eV. PDOSs are the same for the -orbitals of both Co-ions while those of -orbitals are almost the same if x and y-axes are interchanged for two Co-ions. To analyze the spin and orbital configurations, the projected electron occupation numbers are calculated for Co-ions within the muffin-tin radius of 1.25Å. For -orbitals, all spin-up states are almost occupied while only one of the spin-down states is occupied for each Co-type. The doubly occupied -orbital is d for Co-I and d for Co-II. Thus, the Co-ions form an antiferro-orbital ordering and take an intermediate spin state. Such orbital ordering is made possible by the spontaneous Jahn-Teller distortion similar to LaMnO323 (see Supplementary Information). The periodic elongation of CoO6 octahedra along x and y-axes is not only responsible for alternately doubly occupied d and d-orbitals, but also responsible for the different tilting angles along x and y-axes. We would like to emphasize that the Jahn-Teller distortion induced orbital-ordering is a typical feature for all the ground states of SCO/STO superlattices.

Figure 4

The spin and orbital resolved partial densities of states of SCO/STO superlattices at e = 2.3%.

The spin-up PDOSs are plotted upwards while spin-down PDOS are plotted downwards. Other notations are described in the text.

So far, we have obtained a ferroelectric ferromagnetic insulator with large polarization and magnetization. To verify whether such state is a genuine multiferroic state or not, the issues concerning the hysteresis loops for ferroelectricity and ferromagnetism as well as magnetoelectric coupling have to be addressed. While the hysteresis loop for ferroelectricity shows itself automatically by the double well structure, the hysteresis loop for the ferromagnetism has to be demonstrated through the magnetocrystalline anisotropy energy (MAE). By using the algorithms adopted by Xiang et al.27, we compute the MAE of Co-ions of SCO/STO superlattice and the results are presented in Fig. 5a–b. The magnetic anisotropy energies are 0.16 and 0.61 meV at e = 2.3% in the (001) and (100) planes, respectively, which have the same order of magnitude as those of Mn-ions in the good multiferroic compound TbMnO327. Because of the oxygen octahedral tilting, the minima of MAE in (001) plane are located at 35° with respect to a-axis. The minimum of MAE in (100) plane is slightly off the (001) plane and at 93° measuring from c-axis. These data are consistent with the AAFD vector shown in Fig. 2(b) where y component (3.65°) is very close to the easy axis. Magnetoelectric constant can be similarly estimated using the technique devised by Íñiguez28. The dependences of polarization and magnetization as functions of polar-mode distortion are shown in Fig. 5c–d. The polar-mode is chosen as a linear interpolation between the paraelectric P21/c structure and the ferroelectric Pc structure17. The dielectric polarity (q is electron charge) and the magnetic analogue of the dielectric polarity can be extracted from the linear part of P and M. The corresponding eigenvalue C = 15.07 eV/Å2 is obtained from the total energy shown in Fig. 1, and the volume of unit cell is 248.53Å3. The estimated value of magnetoelectric constant is α = 1.44 × 10−3 in Gaussian unit, which is comparable to that of Co3B7O13Br29. To have a reliable magnetoelectric constant, as usual, a high convergence criterion (10−8 eV) is imposed throughout the computations. Thus, the tensile strained SCO/STO superlattices do show excellent multiferroic property with large polarization and magnetization as well as strong magnetoelectric coupling.

Figure 5

The magnetocrystalline anisotropy energy, polarization, and magnetization.

(a)–(b) MAE of Co-ions in the (001) and (100) planes, respectively; (c)–(d) polar-mode distortion dependence of polarization and magnetization. Solid lines refers to P, dotted lines to P = P ΔM = ΔM. Other parameters are described in the text.

Discussion

The robustness of the multiferroic state is checked against the different exchange-correlation functionals and different values of Coulomb repulsion U. As shown in the phase diagram for LDA + U with U = 3.9eV and GGA + U with U = 2.9eV (see Supplementary Information), the strain values for transition points in Fig. 1 may shift somewhat, but the ordering of various ground states are never altered. Thus the overall shape of the phase diagram is independent of the specific exchange-correlation functionals and the specific value of U.

The physical mechanism underlying the multiferroic property of SCO/STO superlattices can be understood from the crystal structure and electron orbital occupation information (see Supplementary Information). The asymmetrical bond lengths around Co- and Ti-ions in the Pc structure demonstrate off-center polar distortion within the CoO6 and TiO6 octahedra. Thus, the electric polarization is contributed by both Co- and Ti-ions. The magnetism comes from the unpaired Co-d electrons. Since Co-ions are responsible for both electric polarization and magnetization, strong magnetoelectric coupling is, of course, expected. With regard to the origin of ferromagnetism in the Pc structure, to the zeroth order, the spin-up states of Co-ions are all occupied while only one of the spin-down states is occupied. The electron occupation is 6 electrons. If we switch to hole picture, the level scheme for holes is just the reverse of level scheme for electrons. In the hole picture, lowest two Co--orbitals and Co--(xy)-orbital are singly occupied by spin-up holes. The nearest neighbor Co--(yz) and -(zx) orbitals are alternatively occupied by a spin-up hole due to antiphase antiferrodistortive tilting of oxygen octahetra. The scenario here is quite similar to LaMnO3 case except the exchange of electrons for holes. AFM state would be favored if the hole occupation is exactly four. Since the exact electron occupation number is large than 6, CoO2 plane is intrinsically electron doped which favors the FM state according to the double exchange mechanism.

We have also extended our study to the generalized (SrCoO3)n/(SrTiO3)m superlattices (n = 1,2,m = 1,2). The numerical analysis suggests that extended superlattice structures do not improve the material properties as a candidate for multiferroic compound. A close proximity between the ferromagnetic SrCoO3 atomic layer and near ferroelectric SrTiO3 atomic layer is the best configuration ensuring the novel multiferroic property. Deviating from this setting will either destabilize the ferromagnetism or favor metallic ground state.

In summary, comprehensive first-principles calculations have been carried out for the electronic and magnetic structures of SCO/STO superlattices and complex phase diagram has been obtained as a function of epitaxial strain. Half-metal and ferromagnetic insulator were discovered in the Pbam structure under compressive strain while a robust multiferroic state was found in tensile strained Pc structure. This ferroelectric ferromagnetic insulator has large polarization and magnetization, and strong magnetoelectric coupling arises from the strong piezoelectric and piezomagnetic coefficients as well as the peculiar orbital ordered structure. The calculated magnetocrystalline anisotropy energy is comparable to that of TbMnO3 while the estimated interface mediated magnetoelectric coupling is comparable to that of Co3B7O13Br. This robust multiferroic state offers an interesting alternative worthy of further experimental investigations.

Methods

Details of numerical computation

In this Report, the electronic structures were studied using a plane wave pseudopotential approach to the density-functional theory30 as implemented in the Vienna ab Initio Simulation Package (VASP)31. We adopt the generalized gradient approximation with Perdew-Burke-Ernzerhof parametrization32 and the Dudarev implementation33 for the on-site Coulomb repulsion U and exchange interaction J. The projector augmented wave potentials34 explicitly include 10 valence electrons for Sr (4s24p65s2), 9 for Co (3d84s1), 12 for Ti (3s23p64s23d2), and 6 for O (2s22p4). The wave functions are expanded in a plane-waves basis with an energy cutoff of 600 eV. A 5 × 5 × 5 Monkhorst-Pack k-point sampling is used for a (20 atoms) unit cell. Each self-consistent electronic calculation is converged to 10−6 eV and the tolerance force is set to 0.005 eV/Å for the ionic relaxation. For Co 3d electrons, U = 1.9eV reproduced the ferromagnetic structure with the correct lattice constant (a = 3.842Å) and magnetic moment (2.967μB) for cubic SrCoO3. This is in agreement with previous theoretical calculations20 and experiment measurements3536. For cubic SrTiO3, a band insulator with the right lattice constant a = 3.940Å is also reproduced. To simulate an epitaxial strain, the in-plane lattice constant (a = b) of a unit cell is fixed while the out-of-plane (c) lattice constant and atomic positions are allowed to relax. The ferroelectric polarization is computed using the Berry-phase approach37.

Author Contributions

W.Y.Z. supervised the work and G.S. carried out the numerical calculations of this work. G.S. and W.Y.Z. both contributed to the analysis and interpretation of results, and the writing of manuscript.