N J Cochrane1, P Shen, Y Yuan, E C Reynolds. 1. Oral Health CRC, Melbourne Dental School, Bio21 Institute, The University of Melbourne, Victoria.
Abstract
BACKGROUND: A range of dental varnishes have been commercialized recently that contain calcium and inorganic phosphate in addition to fluoride. The aim of this study was to analyse the fluoride, calcium and inorganic phosphate ion release from: (1) MI Varnish containing casein phosphopeptide-amorphous calcium phosphate (CPP-ACP); (2) Clinpro White containing functionalized tricalcium phosphate (fTCP); (3) Enamel Pro containing amorphous calcium phosphate; (4) Bifluorid 5 containing calcium fluoride; and (5) Duraphat (no added calcium control). METHODS: The varnishes were applied to a standardized surface area of polyvinyl chloride (n = 7 per group) and immersed in 25 g of distilled deionized water which was changed at 1, 4, 24, 72 and 168 hours. The ion release was determined by ion chromatography and expressed as μmol (cumulative) per gram of varnish. RESULTS: All varnishes released measurable fluoride and calcium, however only MI Varnish and Enamel Pro released significant levels of inorganic phosphate. At 24 hours the order of cumulative fluoride release was: 1>3>4>2=5 with 1 significantly higher (p < 0.05) than the rest. At 72 and 168 hours, the cumulative calcium release was: 1>4>3>2=5 with 1 significantly higher (p < 0.05) than the rest. CONCLUSIONS: MI Varnish containing CPP-ACP had the highest release of calcium and fluoride ions.
BACKGROUND: A range of dental varnishes have been commercialized recently that contain calcium and inorganic phosphate in addition to fluoride. The aim of this study was to analyse the fluoride, calcium and inorganic phosphate ion release from: (1) MI Varnish containing casein phosphopeptide-amorphous calcium phosphate (CPP-ACP); (2) Clinpro White containing functionalized tricalcium phosphate (fTCP); (3) Enamel Pro containing amorphous calcium phosphate; (4) Bifluorid 5 containing calcium fluoride; and (5) Duraphat (no added calcium control). METHODS: The varnishes were applied to a standardized surface area of polyvinyl chloride (n = 7 per group) and immersed in 25 g of distilled deionized water which was changed at 1, 4, 24, 72 and 168 hours. The ion release was determined by ion chromatography and expressed as μmol (cumulative) per gram of varnish. RESULTS: All varnishes released measurable fluoride and calcium, however only MI Varnish and Enamel Pro released significant levels of inorganic phosphate. At 24 hours the order of cumulative fluoride release was: 1>3>4>2=5 with 1 significantly higher (p < 0.05) than the rest. At 72 and 168 hours, the cumulative calcium release was: 1>4>3>2=5 with 1 significantly higher (p < 0.05) than the rest. CONCLUSIONS: MI Varnish containing CPP-ACP had the highest release of calcium and fluoride ions.
Authors: Izabela Świetlicka; Damian Kuc; Michał Świetlicki; Marta Arczewska; Siemowit Muszyński; Ewa Tomaszewska; Adam Prószyński; Krzysztof Gołacki; Jerzy Błaszczak; Krystian Cieślak; Daniel Kamiński; Maria Mielnik-Błaszczak Journal: Biomolecules Date: 2020-05-14
Authors: Ascensión Vicente; Antonio José Ortiz Ruiz; Belén Manuela González Paz; José García López; Luis-Alberto Bravo-González Journal: PLoS One Date: 2017-04-21 Impact factor: 3.240