OBJECTIVE: To determine whether the thickness, processing technique, and cooling protocol of veneer ceramic influence the flexural strength of a bilayer ceramic system. MATERIALS AND METHODS: Sixty-four bar-shaped specimens (20mm×4mm×1mm) of yttria-stabilized tetragonal zirconia (Vita In-Ceram YZ, Vita) were fabricated (ISO 6872) and randomly divided into 8 groups (n=8) according to the factors "processing technique" (P - PM9 and V - VM9), "thickness" (1mm and 3mm), and "cooling protocol" (S - slow and F - fast). The veneer ceramics were applied only over one side of the bar-shaped specimens. All specimens were mechanically cycled (2×10(6) cycles, 84N, 3.4Hz, in water), with the veneer ceramic under tension. Then, the specimens were tested in 4-point bending (1mm/min, load 100kgf, in water), also with the veneer ceramic under tension, and the maximum load was recorded at first sign of fracture. The flexural strength (σ) was calculated, and the mode of failure was determined by stereomicroscopy (30×). The data (MPa) were analyzed statistically by 3-way ANOVA and Tukey's test (α=0.05). RESULTS: ANOVA revealed that the factor "thickness" (p=0.0001) was statistically significant, unlike the factors "processing technique" (p=0.6025) and "cooling protocol" (p=0.4199). The predominant mode of failure was cracking. SIGNIFICANCE: The thickness of the veneer ceramic has an influence on the mechanical strength of the bilayer ceramic system, regardless of processing technique and cooling protocol of the veneer ceramic.
OBJECTIVE: To determine whether the thickness, processing technique, and cooling protocol of veneer ceramic influence the flexural strength of a bilayer ceramic system. MATERIALS AND METHODS: Sixty-four bar-shaped specimens (20mm×4mm×1mm) of yttria-stabilized tetragonal zirconia (Vita In-Ceram YZ, Vita) were fabricated (ISO 6872) and randomly divided into 8 groups (n=8) according to the factors "processing technique" (P - PM9 and V - VM9), "thickness" (1mm and 3mm), and "cooling protocol" (S - slow and F - fast). The veneer ceramics were applied only over one side of the bar-shaped specimens. All specimens were mechanically cycled (2×10(6) cycles, 84N, 3.4Hz, in water), with the veneer ceramic under tension. Then, the specimens were tested in 4-point bending (1mm/min, load 100kgf, in water), also with the veneer ceramic under tension, and the maximum load was recorded at first sign of fracture. The flexural strength (σ) was calculated, and the mode of failure was determined by stereomicroscopy (30×). The data (MPa) were analyzed statistically by 3-way ANOVA and Tukey's test (α=0.05). RESULTS: ANOVA revealed that the factor "thickness" (p=0.0001) was statistically significant, unlike the factors "processing technique" (p=0.6025) and "cooling protocol" (p=0.4199). The predominant mode of failure was cracking. SIGNIFICANCE: The thickness of the veneer ceramic has an influence on the mechanical strength of the bilayer ceramic system, regardless of processing technique and cooling protocol of the veneer ceramic.
Authors: Camila da Silva Rodrigues; Iana Lamadrid Aurélio; Marina da Rosa Kaizer; Yu Zhang; Liliana Gressler May Journal: Dent Mater Date: 2019-03-04 Impact factor: 5.304