Optimizing the concentration of 2,4,6-trimethylbenzoyldiphenylphosphine oxide initiator in composite resins in relation to monomer conversion.

The aim of this study was to optimize the concentration of 2,4,6-trimethylbenzoyldiphenylphosphine oxide (Lucirin® TPO) in unfilled and filled composite resins in relation to the degree of conversion (DC). Increasing concentrations of Lucirin® TPO between 0.05-4.97 wt% were added to equimolar mixtures of Bis-GMA/TEGDMA. Filled resins contained 75 wt% fillers. Standardized samples were cured using a polywave LED light-curing unit (bluephase® G2, Ivoclar Vivadent). Increased initiator concentrations increased logarithmically the DC of unfilled and filled resins. The DC of unfilled resins was in the range of 73-91% at the top and 63-81% at the bottom surfaces and that of filled resins was in the range of 53-81% at the top and 47-70% at the bottom surfaces. The DC in unfilled and filled resins reached a plateau at 1.08 wt% and 1.50 wt% Lucirin® TPO, respectively. Fillers significantly reduced conversion but had no effect on the logarithmic relationship between initiator concentration and the DC.