INTRODUCTION: The aim of the present study was to evaluate the physicochemical properties of a bioceramic root canal sealer, Endosequence BC Sealer. Radiopacity, pH, release of calcium ions (Ca(2+)), and flow were analyzed, and the results were compared with AH Plus cement. METHODS: Radiopacity and flow were evaluated according to ISO 6876/2001 standards. For the radiopacity analysis, metallic rings with 10-mm diameter and 1-mm thickness were filled with cements. The radiopacity value was determined according to radiographic density (mm Al). The flow test was performed with 0.05 mL of cement placed on a glass plate. A 120-g weight was carefully placed over the cement. The largest and smallest diameters of the disks formed were measured by using a digital caliper. The release of Ca(2+) and pH were measured at periods of 3, 24, 72, 168, and 240 hours with spectrophotometer and pH meter, respectively. Data were analyzed by analysis of variance and Tukey test (P < .05). RESULTS: The bioceramic endodontic cement showed radiopacity (3.84 mm Al) significantly lower than that of AH Plus (6.90 mm Al). The pH analysis showed that Endosequence BC Sealer showed pH and release of Ca(2+) greater than those of AH Plus (P < .05) during the experimental periods. The flow test revealed that BC Sealer and AH Plus presented flow of 26.96 mm and 21.17 mm, respectively (P < .05). CONCLUSIONS: Endosequence BC Sealer showed radiopacity and flow according to ISO 6876/2001 recommendations. The other physicochemical properties analyzed demonstrated favorable values for a root canal sealer.
INTRODUCTION: The aim of the present study was to evaluate the physicochemical properties of a bioceramic root canal sealer, Endosequence BC Sealer. Radiopacity, pH, release of calcium ions (Ca(2+)), and flow were analyzed, and the results were compared with AH Plus cement. METHODS: Radiopacity and flow were evaluated according to ISO 6876/2001 standards. For the radiopacity analysis, metallic rings with 10-mm diameter and 1-mm thickness were filled with cements. The radiopacity value was determined according to radiographic density (mm Al). The flow test was performed with 0.05 mL of cement placed on a glass plate. A 120-g weight was carefully placed over the cement. The largest and smallest diameters of the disks formed were measured by using a digital caliper. The release of Ca(2+) and pH were measured at periods of 3, 24, 72, 168, and 240 hours with spectrophotometer and pH meter, respectively. Data were analyzed by analysis of variance and Tukey test (P < .05). RESULTS: The bioceramic endodontic cement showed radiopacity (3.84 mm Al) significantly lower than that of AH Plus (6.90 mm Al). The pH analysis showed that Endosequence BC Sealer showed pH and release of Ca(2+) greater than those of AH Plus (P < .05) during the experimental periods. The flow test revealed that BC Sealer and AH Plus presented flow of 26.96 mm and 21.17 mm, respectively (P < .05). CONCLUSIONS: Endosequence BC Sealer showed radiopacity and flow according to ISO 6876/2001 recommendations. The other physicochemical properties analyzed demonstrated favorable values for a root canal sealer.
Authors: V B Malka; G L Hochscheidt; N L Larentis; F S Grecca; V R C Fontanella; P M P Kopper Journal: Dentomaxillofac Radiol Date: 2015-02-20 Impact factor: 2.419
Authors: Wai Ying Yap; Zeti Adura Che Ab Aziz; Noor Hayati Azami; Afaf Yahya Al-Haddad; Asfand Ali Khan Journal: Med Princ Pract Date: 2017-09-19 Impact factor: 1.927