Mai Mahmoud Yousry1. 1. Department of Restorative Dentistry, Faculty of Oral and Dental Medicine, Cairo University, Egypt. maiyousri@hotmail.com
Abstract
PURPOSE: To determine whether or not re-etching of oxalate-treated dentin and enamel increases microshear bond strength (µSBS) and improves hybridization. MATERIALS AND METHODS: Two single-bottle etch-and-rinse adhesives, SingleBond (3M/ESPE) and OptiBond S (Kerr), were bonded to deep occlusal dentin and enamel after perfusion under 20 mmHg simulated intrapulpal pressure. For each adhesive tested, the experimental groups were: G1: bonding according to manufacturer's instructions (control); G2: application of oxalate desensitizer (D/Sense Crystal, Centrix) to acid-etched substrate followed by 60 s water rinsing prior to bonding; G3: same as G2, but with a further 15-s re-etching with 35% phosphoric acid before bonding. The microshear bond strength (µSBS) to dentin and enamel was tested (n = 15); a scanning electron microscopic (SEM) analysis of surface topography (n = 2), interface (n = 2), and failure mode was also performed. The data were statistically analyzed using ANOVA and Tukey's tests at p ≤ 0.05. RESULTS: In enamel, both adhesives showed no significant difference in μSBS among groups. In dentin, the highest statistically μSBS for both adhesives was recorded for G1, followed by G2, with the lowest values revealed remnants of calcium oxalate crystals that were removed only from enamel surfaces after re-etching. SEM images of the interface revealed inadequate dentin hybridization in G2 and G3 compared to G1. CONCLUSION: Re-etching after oxalate treatment compromises bonding of single-bottle etch-and-rinse adhesives to dentin and provides no added benefits to enamel bonding.
PURPOSE: To determine whether or not re-etching of oxalate-treated dentin and enamel increases microshear bond strength (µSBS) and improves hybridization. MATERIALS AND METHODS: Two single-bottle etch-and-rinse adhesives, SingleBond (3M/ESPE) and OptiBond S (Kerr), were bonded to deep occlusal dentin and enamel after perfusion under 20 mmHg simulated intrapulpal pressure. For each adhesive tested, the experimental groups were: G1: bonding according to manufacturer's instructions (control); G2: application of oxalate desensitizer (D/Sense Crystal, Centrix) to acid-etched substrate followed by 60 s water rinsing prior to bonding; G3: same as G2, but with a further 15-s re-etching with 35% phosphoric acid before bonding. The microshear bond strength (µSBS) to dentin and enamel was tested (n = 15); a scanning electron microscopic (SEM) analysis of surface topography (n = 2), interface (n = 2), and failure mode was also performed. The data were statistically analyzed using ANOVA and Tukey's tests at p ≤ 0.05. RESULTS: In enamel, both adhesives showed no significant difference in μSBS among groups. In dentin, the highest statistically μSBS for both adhesives was recorded for G1, followed by G2, with the lowest values revealed remnants of calcium oxalate crystals that were removed only from enamel surfaces after re-etching. SEM images of the interface revealed inadequate dentin hybridization in G2 and G3 compared to G1. CONCLUSION: Re-etching after oxalate treatment compromises bonding of single-bottle etch-and-rinse adhesives to dentin and provides no added benefits to enamel bonding.
Authors: Nadine Luísa Guimarães Albuquerque; André Mattos Brito de Souza; Maria Denise Rodrigues de Moraes; Juliano Sartori Mendonça; Lidiany Karla Azevedo Rodrigues; Sérgio Lima Santiago Journal: Clin Oral Investig Date: 2015-07-15 Impact factor: 3.573