AIM: To compare physical and mechanical properties of one conventional and one thermomechanically treated nickel-titanium (NiTi) wire used to manufacture rotary endodontic instruments. METHODOLOGY: Two NiTi wires 1.0 mm in diameter were characterized; one of them, C-wire (CW), was processed in the conventional manner, and the other, termed M-Wire (MW), received an additional heat treatment according to the manufacturer. Chemical composition was determined by energy-dispersive X-ray spectroscopy, phase constitution by XRD and the transformation temperatures by DSC. Tensile loading/unloading tests and Vickers microhardness measurements were performed to assess the mechanical behaviour. Data were analysed using analysis of variance (α = 0.05). RESULTS: The two wires showed approximately the same chemical composition, close to the 1 : 1 atomic ratio, and the β-phase was the predominant phase present. B19' martensite and the R-phase were found in MW, in agreement with the higher transformation temperatures found in this wire compared with CW, whose transformation temperatures were below room temperature. Average Vickers microhardness values were similar for MW and CW (P = 0.91). The stress at the transformation plateau in the tensile load-unload curves was lower and more uniform in the M-Wire, which also showed the smallest stress hysteresis and apparent elastic modulus. CONCLUSIONS: The M-Wire had physical and mechanical properties that can render endodontic instruments more flexible and fatigue resistant than those made with conventionally processed NiTi wires.
AIM: To compare physical and mechanical properties of one conventional and one thermomechanically treated nickel-titanium (NiTi) wire used to manufacture rotary endodontic instruments. METHODOLOGY: Two NiTi wires 1.0 mm in diameter were characterized; one of them, C-wire (CW), was processed in the conventional manner, and the other, termed M-Wire (MW), received an additional heat treatment according to the manufacturer. Chemical composition was determined by energy-dispersive X-ray spectroscopy, phase constitution by XRD and the transformation temperatures by DSC. Tensile loading/unloading tests and Vickers microhardness measurements were performed to assess the mechanical behaviour. Data were analysed using analysis of variance (α = 0.05). RESULTS: The two wires showed approximately the same chemical composition, close to the 1 : 1 atomic ratio, and the β-phase was the predominant phase present. B19' martensite and the R-phase were found in MW, in agreement with the higher transformation temperatures found in this wire compared with CW, whose transformation temperatures were below room temperature. Average Vickers microhardness values were similar for MW and CW (P = 0.91). The stress at the transformation plateau in the tensile load-unload curves was lower and more uniform in the M-Wire, which also showed the smallest stress hysteresis and apparent elastic modulus. CONCLUSIONS: The M-Wire had physical and mechanical properties that can render endodontic instruments more flexible and fatigue resistant than those made with conventionally processed NiTi wires.
Authors: N Tulasi Priya; Veeramachaneni Chandrasekhar; S Anita; Muralidhar Tummala; T B Phanindhar Raj; Vijetha Badami; Pradeep Kumar; E Soujanya Journal: J Clin Diagn Res Date: 2014-12-05
Authors: Javier Gil; Elisa Rupérez; Eugenio Velasco; Conrado Aparicio; José María Manero Journal: J Mater Sci Mater Med Date: 2018-08-07 Impact factor: 3.896
Authors: Chiara Pirani; Oddone Ruggeri; Pier Paolo Cirulli; Gian Andrea Pelliccioni; Maria Giovanna Gandolfi; Carlo Prati Journal: Odontology Date: 2013-04-09 Impact factor: 2.634
Authors: Gabriele Miccoli; Gianfranco Gaimari; Marco Seracchiani; Antonio Morese; Tatyana Khrenova; Dario Di Nardo Journal: Ann Stomatol (Roma) Date: 2017-11-08