Peter Tschoppe1, Daniela L Zandim, Peter Martus, Andrej M Kielbassa. 1. Department of Operative Dentistry and Periodontology, University School of Dental Medicine, CharitéCentrum 3, Charité - Universitätsmedizin Berlin, Aßmannshauser Strasse 4-6, D-14197 Berlin, Germany.
Abstract
OBJECTIVES: This in vitro study evaluated the effects of nano-hydroxyapatite (n-HAp) toothpastes on remineralization of bovine enamel and dentine subsurface lesions. METHODS: Specimens were demineralized, randomly divided into five groups, and exposed to an aqueous remineralizing solution for two and five weeks (37 °C). Brushing procedures were performed with the respective toothpaste/storage solution slurry twice daily (2 × 5 s; total contact time of the slurries 2 × 120s/d): storage in remineralizing solution only (0); additional brushing with B (20 wt% zinc carbonate nano-hydroxyapatite, ZnCO(3)/n-HAp); BS (24 wt% ZnCO(3)/n-HAp); E (0.14 wt% amine fluoride); or A (7 wt% pure n-HAp). Differences in mineral loss (ΔΔZ) before and after storage/treatment were microradiographically evaluated. RESULTS: Dentine groups 0, B, BS, and A showed significantly higher ΔΔZ values compared to E (p < 0.05; ANOVA). Enamel ΔΔZ values of group A were significantly higher compared to group E (p < 0.05), whilst no significant differences of these groups could be observed compared to 0, B, and BS (p > 0.05). CONCLUSIONS: With the in vitro conditions chosen, toothpastes containing n-HAp revealed higher remineralizing effects compared to amine fluoride toothpastes with bovine dentine, and comparable trends were obtained for enamel.
OBJECTIVES: This in vitro study evaluated the effects of nano-hydroxyapatite (n-HAp) toothpastes on remineralization of bovine enamel and dentine subsurface lesions. METHODS: Specimens were demineralized, randomly divided into five groups, and exposed to an aqueous remineralizing solution for two and five weeks (37 °C). Brushing procedures were performed with the respective toothpaste/storage solution slurry twice daily (2 × 5 s; total contact time of the slurries 2 × 120s/d): storage in remineralizing solution only (0); additional brushing with B (20 wt% zinc carbonate nano-hydroxyapatite, ZnCO(3)/n-HAp); BS (24 wt% ZnCO(3)/n-HAp); E (0.14 wt% amine fluoride); or A (7 wt% pure n-HAp). Differences in mineral loss (ΔΔZ) before and after storage/treatment were microradiographically evaluated. RESULTS: Dentine groups 0, B, BS, and A showed significantly higher ΔΔZ values compared to E (p < 0.05; ANOVA). Enamel ΔΔZ values of group A were significantly higher compared to group E (p < 0.05), whilst no significant differences of these groups could be observed compared to 0, B, and BS (p > 0.05). CONCLUSIONS: With the in vitro conditions chosen, toothpastes containing n-HAp revealed higher remineralizing effects compared to amine fluoride toothpastes with bovine dentine, and comparable trends were obtained for enamel.
Authors: M Esteves-Oliveira; N M Santos; H Meyer-Lueckel; R J Wierichs; J A Rodrigues Journal: Clin Oral Investig Date: 2016-03-19 Impact factor: 3.573