OBJECTIVE: The objective of this study was to determine the capability of silk fibroin powder as a biomaterial template for the restoration of peri-implant defects when mixed with Choukroun platelet-rich fibrin (PRF) in vivo. STUDY DESIGN: Ten New Zealand white rabbits were used for this study. Using a trephine bur (diameter 7.0 mm), 2 monocortical defects were prepared. Subsequently, 2 dental implants were installed into the tibia (diameter 3.0 mm, length 10.0 mm). In the experimental group, the peri-implant defect was filled with a combination graft of silk fibroin powder and Choukroun PRF. The control was left in an unfilled state. The animals were killed at 8 weeks. Subsequently, a removal torque test and a histomorphometric analysis were done. RESULTS: The removal torque for the experimental group was 30.34 +/- 5.06 N.cm, whereas it was 21.86 +/- 3.39 N.cm for the control. The difference between the 2 groups was statistically significant (P = .010). Mean new bone formation was 51.93 +/- 27.90% in the experimental group and 11.67 +/- 15.12% in the control (P = .003). Mean bone-to-implant contact was 43.07 +/- 21.96% in the experimental group and 15.37 +/- 23.84% in the control (P = .002). CONCLUSION: A peri-implant defect can be successfully repaired by the application of Choukroun PRF and silk fibroin powder. Copyright 2010 Mosby, Inc. All rights reserved.
OBJECTIVE: The objective of this study was to determine the capability of silk fibroin powder as a biomaterial template for the restoration of peri-implant defects when mixed with Choukroun platelet-rich fibrin (PRF) in vivo. STUDY DESIGN: Ten New Zealand white rabbits were used for this study. Using a trephine bur (diameter 7.0 mm), 2 monocortical defects were prepared. Subsequently, 2 dental implants were installed into the tibia (diameter 3.0 mm, length 10.0 mm). In the experimental group, the peri-implant defect was filled with a combination graft of silk fibroin powder and Choukroun PRF. The control was left in an unfilled state. The animals were killed at 8 weeks. Subsequently, a removal torque test and a histomorphometric analysis were done. RESULTS: The removal torque for the experimental group was 30.34 +/- 5.06 N.cm, whereas it was 21.86 +/- 3.39 N.cm for the control. The difference between the 2 groups was statistically significant (P = .010). Mean new bone formation was 51.93 +/- 27.90% in the experimental group and 11.67 +/- 15.12% in the control (P = .003). Mean bone-to-implant contact was 43.07 +/- 21.96% in the experimental group and 15.37 +/- 23.84% in the control (P = .002). CONCLUSION: A peri-implant defect can be successfully repaired by the application of Choukroun PRF and silk fibroin powder. Copyright 2010 Mosby, Inc. All rights reserved.