Enhanced cell ingrowth and proliferation through three-dimensional nanocomposite scaffolds with controlled pore structures.

We present enhanced cell ingrowth and proliferation through cross-linked three-dimensional (3D) nanocomposite scaffolds fabricated using poly(propylene fumarate) (PPF) and hydroxyapatite (HA) nanoparticles. Scaffolds with controlled internal pore structures were produced from computer-aided design (CAD) models and solid freeform fabrication (SFF) technique, while those with random pore structures were fabricated by a NaCl leaching technique for comparison. The morphology and mechanical properties of scaffolds were characterized using scanning electron microscopy (SEM) and mechanical testing, respectively. Pore interconnectivity of scaffolds was assessed using X-ray microcomputed tomography (micro-CT) and 3D imaging analysis. In vitro cell studies have been performed using MC3T3-E1 mouse preosteoblasts and cultured scaffolds in a rotating-wall-vessel bioreactor for 4 and 7 days to assess cell attachment, viability, ingrowth depth, and proliferation. The mechanical properties of cross-linked nanocomposite scaffolds were not significantly different after adding HA or varying pore structures. However, pore interconnectivity of PPF/HA nanocomposite scaffolds with controlled pore structures has been significantly increased, resulting in enhanced cell ingrowth depth 7 days after cell seeding. Cell attachment and proliferation are also higher in PPF/HA nanocomposite scaffolds. These results suggest that cross-linked PPF/HA nanocomposite scaffolds with controlled pore structures may lead to promising bone tissue engineering scaffolds with excellent cell proliferation and ingrowth.