STATEMENT OF THE PROBLEM: Light-curing of resin-based composites (RBCs) is associated with temperature increase in the pulp chamber, which may have a detrimental effect on the vital pulp. PURPOSE: The purpose of the study was to evaluate temperature changes of silorane-, ormocer-, and dimethacrylate-based RBCs at the bottom surface of the RBC and in the pulp chamber roof dentin (PCRD) during curing. MATERIALS AND METHODS: In part A, temperatures were measured for Filtek LS (3M ESPE, St. Paul, MN, USA), Admira (Voco GmbH, Cuxhaven, Germany), and Herculite XRV (Kerr Corp., Orange, CA, USA) with a high-power light-emitting diode (LED) unit by placing thermocouples in contact with the bottom surface of the material in standardized acrylic molds. In part B, temperature changes in PCRD were measured in extracted molars during light-curing of adhesives and RBCs in 2-mm-deep cavities with a remaining dentin thickness (RDT) of 1 mm. RESULTS: Filtek LS showed a different temperature curve compared with Admira and Herculite XRV. Significantly higher temperatures were recorded for Filtek LS (p < 0.001) than for Admira and Herculite XRV in acrylic molds. Temperature rises recorded in PCRD for adhesives and RBCs were between 4.1 and 6.4 degrees C. No significant differences in PCRD temperatures were found between the three groups during adhesive curing and RBC curing (p > 0.05). CONCLUSIONS: Filtek LS showed a different heat-generation pattern from and significantly higher temperatures than Admira and Herculite XRV when the materials were tested in acrylic molds. Similar temperatures were recorded in the PCRD during curing of adhesives and RBCs. CLINICAL SIGNIFICANCE: Although a substantial temperature rise in the bulk material occurred during light-curing of the three resin-based composites, a remaining dentin thickness of 1 mm caused a significant reduction in pulp chamber roof dentin temperatures. Temperatures measured in the pulp chamber roof dentin corresponding to the zone occupied by the postmitotic odontoblast layer were not statistically different for the three types of resin-based composites.
STATEMENT OF THE PROBLEM: Light-curing of resin-based composites (RBCs) is associated with temperature increase in the pulp chamber, which may have a detrimental effect on the vital pulp. PURPOSE: The purpose of the study was to evaluate temperature changes of silorane-, ormocer-, and dimethacrylate-based RBCs at the bottom surface of the RBC and in the pulp chamber roof dentin (PCRD) during curing. MATERIALS AND METHODS: In part A, temperatures were measured for Filtek LS (3M ESPE, St. Paul, MN, USA), Admira (Voco GmbH, Cuxhaven, Germany), and Herculite XRV (Kerr Corp., Orange, CA, USA) with a high-power light-emitting diode (LED) unit by placing thermocouples in contact with the bottom surface of the material in standardized acrylic molds. In part B, temperature changes in PCRD were measured in extracted molars during light-curing of adhesives and RBCs in 2-mm-deep cavities with a remaining dentin thickness (RDT) of 1 mm. RESULTS: Filtek LS showed a different temperature curve compared with Admira and Herculite XRV. Significantly higher temperatures were recorded for Filtek LS (p < 0.001) than for Admira and Herculite XRV in acrylic molds. Temperature rises recorded in PCRD for adhesives and RBCs were between 4.1 and 6.4 degrees C. No significant differences in PCRD temperatures were found between the three groups during adhesive curing and RBC curing (p > 0.05). CONCLUSIONS: Filtek LS showed a different heat-generation pattern from and significantly higher temperatures than Admira and Herculite XRV when the materials were tested in acrylic molds. Similar temperatures were recorded in the PCRD during curing of adhesives and RBCs. CLINICAL SIGNIFICANCE: Although a substantial temperature rise in the bulk material occurred during light-curing of the three resin-based composites, a remaining dentin thickness of 1 mm caused a significant reduction in pulp chamber roof dentin temperatures. Temperatures measured in the pulp chamber roof dentin corresponding to the zone occupied by the postmitotic odontoblast layer were not statistically different for the three types of resin-based composites.
Authors: Maciej Janeczek; Katarzyna Herman; Katarzyna Fita; Krzysztof Dudek; Małgorzata Kowalczyk-Zając; Agnieszka Czajczyńska-Waszkiewicz; Dagmara Piesiak-Pańczyszyn; Piotr Kosior; Maciej Dobrzyński Journal: Biomed Res Int Date: 2016-10-20 Impact factor: 3.411