PURPOSE: The aim of this in vitro study was to evaluate the tensile strength of titanium cylinders cemented on stainless steel abutment mock-ups by the Cerazone system. METHODS AND MATERIALS: Four types of cements were used: glass ionomer, Fuji I (GC); zinc phosphate, Cimento LS (Vigodent); zinc oxide without eugenol, Rely x Temp NE (3M ESPE); and resin cement, Rely x ARC (3M ESPE). Four experimental groups were formed, each composed of 5 test specimens. Each test specimen consisted of a set of 1 cylinder and 1 stainless steel abutment mock-up. All cements tested were manipulated in accordance with manufacturers' instructions. A static load of 5 Newtons (N) for 2 minutes was used to standardize the procedure. The tensile tests were performed by a mechanical universal testing machine (EMIC DL500MF) at a crosshead speed of 0.5 mm/min. RESULTS: The highest bonding values resulting from the experiment were obtained by Cimento LS (21.86 MPa mean), followed by the resin cement Rely x ARC (12.95 MPa mean), Fuji I (6.89 MPa mean), and Rely x Temp NE (4.71 MPa mean). The results were subjected to analysis of variance (ANOVA) and the Student's t test. CONCLUSION: The cements differed amongst them as regards tensile strength, with the highest bonding levels recorded with zinc phosphate (Cimento LS) and the lowest with the zinc oxide without eugenol (Rely x Temp NE).
PURPOSE: The aim of this in vitro study was to evaluate the tensile strength of titanium cylinders cemented on stainless steel abutment mock-ups by the Cerazone system. METHODS AND MATERIALS: Four types of cements were used: glass ionomer, Fuji I (GC); zinc phosphate, Cimento LS (Vigodent); zinc oxide without eugenol, Rely x Temp NE (3M ESPE); and resin cement, Rely x ARC (3M ESPE). Four experimental groups were formed, each composed of 5 test specimens. Each test specimen consisted of a set of 1 cylinder and 1 stainless steel abutment mock-up. All cements tested were manipulated in accordance with manufacturers' instructions. A static load of 5 Newtons (N) for 2 minutes was used to standardize the procedure. The tensile tests were performed by a mechanical universal testing machine (EMIC DL500MF) at a crosshead speed of 0.5 mm/min. RESULTS: The highest bonding values resulting from the experiment were obtained by Cimento LS (21.86 MPa mean), followed by the resin cement Rely x ARC (12.95 MPa mean), Fuji I (6.89 MPa mean), and Rely x Temp NE (4.71 MPa mean). The results were subjected to analysis of variance (ANOVA) and the Student's t test. CONCLUSION: The cements differed amongst them as regards tensile strength, with the highest bonding levels recorded with zinc phosphate (Cimento LS) and the lowest with the zinc oxide without eugenol (Rely x Temp NE).