Influence of air abrasion and long-term storage on the bond strength of self-etching adhesives to dentin.

This study tested the effects of long-term storage and aluminum oxide air abrasion on the bond strength of self-etching adhesive systems. Extracted human third molars were ground flat with 600-grit SiC paper to expose middle coronal dentin. Clearfil SE Bond and One-Up Bond F were applied to dentin surfaces in accordance with manufacturers instructions with or without previous aluminum oxide 50 microm air abrasion. A crown was built up with the resin composite TPH Spectrum and the specimens were stored in water for 24 hours. The bonded assemblies were vertically sectioned into beams for microtensile bond testing. The beams of each tooth were individually immersed in bottles containing water at 37 degrees C for one day, three and six months; the water was changed daily. The specimens were then subjected to microtensile bond testing. The bond strength data were subjected to ANOVA and Tukey Kramer test. Fractured specimens were analyzed in a scanning electron microscope to determine failure modes. Air abrasion improved Clearfil SE Bond bond strength in the three month evaluation. No significant difference was found between the two adhesives systems, but bond strengths gradually decreased over time. Failure modes varied significantly among groups and were influenced by long-term storage and aluminum oxide air abrasion.