Influence of Nd:YAG laser irradiation on an adhesive restorative procedure.

Hard tissue modification by means of laser irradiation is becoming popular in dentistry, since it promotes assorted responses between the tooth and the restorative material. Some studies on the bond strength of adhesive systems to Nd:YAG irradiated teeth have shown distinctive behaviors when irradiation was applied before or after the adhesive agent. This study evaluated the microtensile bond strength of a commercial adhesive system to dentin irradiated with Nd:YAG laser after adhesive application but prior to polymerization. The experiment was conducted in vitro, using freshly extracted human teeth as samples. For the microtensile test, the teeth were separated into 4 different groups according to the energy density of laser irradiation: 0, 5, 10 and 50 J/cm2. The data was analyzed with analysis of variance (ANOVA) and LSD tests, and the results indicated that the group that was irradiated with 5 J/cm2 had significantly higher bond strength values. Adhesive penetration on the etched dentin was observed by scanning electron microscopy, where the images showed better adhesive penetration on dentinal tubules after dentin irradiation with 5 J/cm2. Based on the results of this study, it is possible to conclude that irradiation of dentin with the Nd:YAG laser at low energy densities after application of the adhesive but prior to polymerization might be positive for the adhesive restorative process.