OBJECTIVE: This study evaluated the shear bond strength of two resin composite luting cements to zirconium oxide ceramic substrate using two air-particle abrasion methods. METHODS: Two resin composite cements, RelyX Unicem (3M ESPE) and Panavia F (Kuraray), each with an acidic composition, were used in combination with a zirconium oxide (DCS Dental AG) substrate containing Al2O3 and SiO2 (Rocatec system, 3M ESPE) and two air-particle abrasion methods. The shear bond strength of the resin composite cement to the substrate was tested after the samples were either water-stored for one week or thermocycled following 24 hours of water storage. RESULTS: The RelyX Unicem resin composite cement specimens with the Rocatec treatment (20.9 +/- 4.6 Mpa and 20.1 +/- 4.2 MPa, respectively, n = 12) demonstrated the highest shear bond strength. Alternatively, the lowest values were obtained for the Panavia F resin cement samples, with Al2O3 air-particle abrasion in both storage conditions, water storage for one week (17.7 +/- 8.9MPa) or thermocycling after 24 hours of water storage (16.3 +/- 4.9 MPa). Neither storage condition or particle abrasion system significantly affected shear bond strengths (ANOVA, p > 0.05). CONCLUSION: It was concluded that two different surface conditioning methods and storage conditions did not significantly affect the bonding properties of Panavia F and RelyX Unicem resin composite luting cements to Zirconia.
OBJECTIVE: This study evaluated the shear bond strength of two resin composite luting cements to zirconium oxide ceramic substrate using two air-particle abrasion methods. METHODS: Two resin composite cements, RelyX Unicem (3M ESPE) and Panavia F (Kuraray), each with an acidic composition, were used in combination with a zirconium oxide (DCS Dental AG) substrate containing Al2O3 and SiO2 (Rocatec system, 3M ESPE) and two air-particle abrasion methods. The shear bond strength of the resin composite cement to the substrate was tested after the samples were either water-stored for one week or thermocycled following 24 hours of water storage. RESULTS: The RelyX Unicem resin composite cement specimens with the Rocatec treatment (20.9 +/- 4.6 Mpa and 20.1 +/- 4.2 MPa, respectively, n = 12) demonstrated the highest shear bond strength. Alternatively, the lowest values were obtained for the Panavia F resin cement samples, with Al2O3 air-particle abrasion in both storage conditions, water storage for one week (17.7 +/- 8.9MPa) or thermocycling after 24 hours of water storage (16.3 +/- 4.9 MPa). Neither storage condition or particle abrasion system significantly affected shear bond strengths (ANOVA, p > 0.05). CONCLUSION: It was concluded that two different surface conditioning methods and storage conditions did not significantly affect the bonding properties of Panavia F and RelyX Unicem resin composite luting cements to Zirconia.
Authors: Leonardo C Zeidan; Camila M Esteves; Juliana A Oliveira; Aldo Brugnera; Alessandra Cassoni; José Augusto Rodrigues Journal: Lasers Med Sci Date: 2017-10-27 Impact factor: 3.161
Authors: Markus B Blatz; Jin-Ho Phark; Fusun Ozer; Francis K Mante; Najeed Saleh; Michael Bergler; Avishai Sadan Journal: Clin Oral Investig Date: 2009-05-05 Impact factor: 3.573