Effect of spatial architecture on cellular colonization.

The spatial cell-material interaction remains vital issue in forming biodegradable scaffolds in Tissue Engineering. In this study, to understand the influence of spatial architecture on cellular behavior, 2D and 3D chitosan scaffolds of 50-190 kD and >310 kD MW were synthesized through air drying and controlled rate freezing/lypohilization technique, respectively. In addition, chitosan was emulsified with 19, 76, and 160 kD 50:50 poly lactide-co-glycolide (PLGA) using 1,2-Dimyristoyl-sn-Glycero-3-Phosphocholine (DMPC) as stabilizer. 2D and 3D scaffolds were formed by air drying and lyophilization as before. Tensile and compressive properties of films and scaffolds were analyzed in wet conditions at 37 degrees C. Alterations in the cell spreading, proliferation, and cytoskeletal organization of human umbilical vein endothelial cells (HUVECs) and mouse embryonic fibroblasts (MEFs) were studied. These results showed that the formed 3D chitosan scaffolds had interconnected open pore architecture (50-200 microm size). HUVECs and MEFs had reduced spreading areas and circular morphology on 2D chitosan membranes compared with 3D chitosan scaffolds. The fluorescence photomicrographs for actin (using Alexa Fluor 488 phalloidin) and cytoplasm staining (using carboxyfluorescein diacetate-succinimidyl ester) demonstrated that the cells spread within 3D chitosan matrix. 2D and 3D emulsified chitosan and chitosan/PLGA scaffolds reduced the spreading of HUVECs and MEFs even further. Proliferation results, analyzed via MTT-Formazan assay and BrdU uptake assay, correlated with the spreading characteristics. The reductions in cell spreading area on emulsified surfaces were not detrimental to the viability and endocytic activity but to proliferation. The observed alterations in cellular colonization are in part due to the substrate stiffness and surface topography. In summary, these results suggest a significant influence of spatial architecture on cellular colonization.