C R A Valois1, L P Silva, R B Azevedo. 1. Department of Genetics and Morphology, Institute of Biology, University of Brasília, Brasília, Brazil.
Abstract
AIM: To compare the effects of 2% chlorhexidine (CHX) and 5.25% sodium hypochlorite (NaOCl) on gutta-percha (GP) cone structure using atomic force microscopy (AFM). METHODOLOGY: Two standardized GP cones were sectioned 3 mm from the tip, attached to a glass base and immersed in 2% CHX or 5.25% NaOCl for 1, 5, 10, 20 and 30 min. Untreated GP cones were used as control. Topography and elasticity analyses were performed on 12 different regions located between 1 and 2 mm from the tip. Root mean square (RMS) parameters for contact mode imaging and force modulation microscopy variations were measured. The differences between RMS values were tested by anova with Fisher's protected LSD test for multiple comparisons. RESULTS: There was no deterioration in the topography and physical properties studied when 2% CHX was used in comparison with the control (P < 0.05). The RMS parameter for topography increased after 10 min of 5.25% NaOCl exposure in comparison with the control (P < 0.05). In addition, 5.25% NaOCl increased the elasticity of the GP cone after an immersion time of 1 min in comparison with the control (P < 0.05). CONCLUSIONS: Two per cent CHX did not change GP cone structure following up to 30 min exposure. Conversely, 5.25% NaOCl caused elastic changes after 1 min exposure.
AIM: To compare the effects of 2% chlorhexidine (CHX) and 5.25% sodium hypochlorite (NaOCl) on gutta-percha (GP) cone structure using atomic force microscopy (AFM). METHODOLOGY: Two standardized GP cones were sectioned 3 mm from the tip, attached to a glass base and immersed in 2% CHX or 5.25% NaOCl for 1, 5, 10, 20 and 30 min. Untreated GP cones were used as control. Topography and elasticity analyses were performed on 12 different regions located between 1 and 2 mm from the tip. Root mean square (RMS) parameters for contact mode imaging and force modulation microscopy variations were measured. The differences between RMS values were tested by anova with Fisher's protected LSD test for multiple comparisons. RESULTS: There was no deterioration in the topography and physical properties studied when 2% CHX was used in comparison with the control (P < 0.05). The RMS parameter for topography increased after 10 min of 5.25% NaOCl exposure in comparison with the control (P < 0.05). In addition, 5.25% NaOCl increased the elasticity of the GP cone after an immersion time of 1 min in comparison with the control (P < 0.05). CONCLUSIONS: Two per cent CHX did not change GP cone structure following up to 30 min exposure. Conversely, 5.25% NaOCl caused elastic changes after 1 min exposure.