OBJECTIVES: The aim of this study was to investigate the influence of new diluent agents, diluent ratio and filler content, on relevant mechanical properties of several novel composite resins containing Bis-GMA as resin matrices, and to compare these with the properties of composites based on TEGDMA, a conventionally used diluent. METHODS: Two Bis-GMA analogues were synthesized and 20 experimental composite resins were prepared combining three monomer mixtures (Bis-GMA/TEGDMA, Bis-GMA/CH3 Bis-GMA and Bis-GMA/CF3 Bis-GMA), at three dilution rates (85/15, 10/90, 0/100) and three levels of hybrid filler content (barium aluminosilicate glass): 0, 10 and 35%. Flexural strength (FS), modulus of elasticity (ME) and microhardness (VHN) of the composites were evaluated. Five specimens of each material were prepared for each mechanical test, light-cured over 120 s and stored in water at 37 degrees C for 1 week. Three-point bending test was used for FS measurement and VHN was quantified by using a Vickers microindentor. Data were analyzed by ANOVA and Student-Newman-Keuls tests (P<0.05). RESULTS: Materials with CH3 Bis-GMA showed an enhanced VHN. Mean FS was higher for matrices containing TEGDMA. Overall, dilution favored FS and VHN but not ME. Filler loading specially improved ME and VHN. SIGNIFICANCE: Results correlate with an increase in the extent of polymerization due to the higher flexibility of the less viscous comonomer starting system and the hydrophobic character of the Bis-GMA analogues.
OBJECTIVES: The aim of this study was to investigate the influence of new diluent agents, diluent ratio and filler content, on relevant mechanical properties of several novel composite resins containing Bis-GMA as resin matrices, and to compare these with the properties of composites based on TEGDMA, a conventionally used diluent. METHODS: Two Bis-GMA analogues were synthesized and 20 experimental composite resins were prepared combining three monomer mixtures (Bis-GMA/TEGDMA, Bis-GMA/CH3 Bis-GMA and Bis-GMA/CF3 Bis-GMA), at three dilution rates (85/15, 10/90, 0/100) and three levels of hybrid filler content (barium aluminosilicate glass): 0, 10 and 35%. Flexural strength (FS), modulus of elasticity (ME) and microhardness (VHN) of the composites were evaluated. Five specimens of each material were prepared for each mechanical test, light-cured over 120 s and stored in water at 37 degrees C for 1 week. Three-point bending test was used for FS measurement and VHN was quantified by using a Vickers microindentor. Data were analyzed by ANOVA and Student-Newman-Keuls tests (P<0.05). RESULTS: Materials with CH3 Bis-GMA showed an enhanced VHN. Mean FS was higher for matrices containing TEGDMA. Overall, dilution favored FS and VHN but not ME. Filler loading specially improved ME and VHN. SIGNIFICANCE: Results correlate with an increase in the extent of polymerization due to the higher flexibility of the less viscous comonomer starting system and the hydrophobic character of the Bis-GMA analogues.
Authors: Jasmine Sinha; Adam Dobson; Osamah Bankhar; Maciej Podgórski; Parag K Shah; Sheryl L W Zajdowicz; Abdulaziz Alotaibi; Jeffrey W Stansbury; Christopher N Bowman Journal: Dent Mater Date: 2019-11-30 Impact factor: 5.304