Bioactive nanocrystalline sol-gel hydroxyapatite coatings.

Sol-gel technology offers an alternative technique for producing bioactive surfaces for improved bone attachment. Previous work indicated that monophasic hydroxyapatite coatings were difficult to produce. In the present work hydroxyapatite was synthesized using the sol-gel technique with alkoxide precursors and the solution was allowed to age up to seven days prior to coating. It was found that, similar to the wet-chemical method of hydroxyapatite powder synthesis, an aging time is required to produce a pure hydroxyapatite phase. A methodology that has been successfully used to produce nanocrystalline hydroxyapatite thin film coatings via the sol-gel route on various substrates including alumina, Vycor glass, partially stabilized zirconia, Ti-6Al-4V alloy and single crystal MgO is described. Coatings produced on MgO substrates were characterized by X-ray diffraction and atomic force microscopy, while the analogous gels were examined with thermogravimetric and differential thermal analyses. The coatings were crack free and the surface was covered with small grains, of approximately 200 nm in size for samples fired to 1000 degrees C. Coating thickness varied between 70 and 1000 nm depending on the number of applied layers. Copyright 1999 Kluwer Academic Publishers