Jérôme Chevalier1, Sylvain Deville, Etienne Münch, Romain Jullian, Frédéric Lair.
Abstract
The isothermal tetragonal-to-monoclinic transformation of 3Y-TZP ceramics sintered at two different temperatures (1450 degrees C and 1550 degrees C) and duration (2 and 5h) is investigated at 134 degrees C in steam. Particular attention is paid to the presence of a cubic phase and its effect on isothermal aging. Sintering at 1550 degrees C can result in a significant amount of large cubic grains in the specimens, that have a detrimental impact on aging resistance, especially for the first stage of the aging process. Cubic grains appear to be enriched in yttrium, which in turn leads to a depletion of yttrium in the neighboring tetragonal grains. These grains will act as nucleation sites for tetragonal-to-monoclinic transformation. Even for specimens sintered at lower temperature, i.e. 1450 degrees C, the presence of a cubic phase is expected from the phase diagram, leading to a significant effect on aging sensitivity.Entities:
Mesh：
Substances：
Year: 2004 PMID： 15142736 DOI： 10.1016/j.biomaterials.2004.01.002
Source DB: PubMed Journal: Biomaterials ISSN： 0142-9612 Impact factor: 12.479