Formation behavior of PCDD/Fs in PVC pyrolysis with copper oxide.

Formation and decomposition behaviors of PCDD/Fs during pyrolysis of polyvinyl chloride (PVC) with CuO have been investigated. These reactions proceed simultaneously, and the rate of decomposition exceeds that of formation with further retention. More 2,3,7,8-TCDD is formed when the dechlorination of PCDD/Fs proceeds significantly. Homologue profile patterns of PCDD/Fs show that the fractions of O8CDD and H6CDFs are relatively larger within PCDDs and PCDFs, respectively. Extremely large amounts of PCDD/Fs are obtained with the long retention time at 200 degrees C. The formation of PCDD/Fs decreases drastically with increase in the molar ratio of CuO/PVC. The acceptability of thermodynamic calculations on the formation of PCDD/Fs is also investigated. The thermodynamic calculated tendency of the effect of oxygen on the formation of PCDD/Fs agrees well with the experimental results, although absolute values of the amount of PCDD/Fs are much different.