J Nissan1, Y Dmitry, D Assif. 1. Department of Prosthetic Dentistry, The Maurice and Gabriela Goldschleger School of Dental Medicine, Tel Aviv University, Tel Aviv, Israel. nissandr@post.tau.ac.il
Abstract
STATEMENT OF PROBLEM: Cements that yield high retentive values are believed to allow use of shorter posts. PURPOSE: This study investigated the use of reinforced composite resin cement as compensation for reduced dowel length. MATERIAL AND METHODS: The retention values of stainless steel posts (parallel-sided ParaPost and tapered Dentatus in 5-, 8-, and 10-mm lengths) luted with Flexi-Flow titanium-reinforced composite resin and zinc phosphate cements were evaluated. Single-rooted extracted human teeth with crowns (n = 120), removed at the cementoenamel junction, were randomly divided into 4 groups of 30 samples each. Different post lengths were luted with either Flexi-Flow or zinc phosphate. Each sample was placed into a specialized jig and on a tensile testing machine with a crosshead speed of 2 mm/min, applied until failure. The effect of different posts and cements on the force required to dislodge the dowels was evaluated with multiple analyses of variance (ANOVA). One-way ANOVA with Scheffé contrast was applied to determine the effect of different post lengths on the retentive failure of posts luted with the 2 agents. RESULTS: Flexi-Flow reinforced composite resin cement significantly increased retention of ParaPost and Dentatus dowels (P<.001) compared with zinc phosphate. One-way ANOVA revealed no statistically significant difference (P>.05) between mean retention of both dowels luted with Flexi-Flow for all posts length used (5 mm = 8 mm = 10 mm). Mean retention values of the groups luted with zinc phosphate showed a statistically significant difference (P<.001) for the different post lengths (10 > 8 > 5 mm). Parallel-sided ParaPost dowels demonstrated a higher mean retention than tapered Dentatus dowels (P<.001). CONCLUSION: In this study, Flexi-Flow reinforced composite resin cement compensated for the reduced length of shorter parallel-sided ParaPost and tapered Dentatus dowels.
RCT Entities:
STATEMENT OF PROBLEM: Cements that yield high retentive values are believed to allow use of shorter posts. PURPOSE: This study investigated the use of reinforced composite resin cement as compensation for reduced dowel length. MATERIAL AND METHODS: The retention values of stainless steel posts (parallel-sided ParaPost and tapered Dentatus in 5-, 8-, and 10-mm lengths) luted with Flexi-Flow titanium-reinforced composite resin and zinc phosphate cements were evaluated. Single-rooted extracted human teeth with crowns (n = 120), removed at the cementoenamel junction, were randomly divided into 4 groups of 30 samples each. Different post lengths were luted with either Flexi-Flow or zinc phosphate. Each sample was placed into a specialized jig and on a tensile testing machine with a crosshead speed of 2 mm/min, applied until failure. The effect of different posts and cements on the force required to dislodge the dowels was evaluated with multiple analyses of variance (ANOVA). One-way ANOVA with Scheffé contrast was applied to determine the effect of different post lengths on the retentive failure of posts luted with the 2 agents. RESULTS: Flexi-Flow reinforced composite resin cement significantly increased retention of ParaPost and Dentatus dowels (P<.001) compared with zinc phosphate. One-way ANOVA revealed no statistically significant difference (P>.05) between mean retention of both dowels luted with Flexi-Flow for all posts length used (5 mm = 8 mm = 10 mm). Mean retention values of the groups luted with zinc phosphate showed a statistically significant difference (P<.001) for the different post lengths (10 > 8 > 5 mm). Parallel-sided ParaPost dowels demonstrated a higher mean retention than tapered Dentatus dowels (P<.001). CONCLUSION: In this study, Flexi-Flow reinforced composite resin cement compensated for the reduced length of shorter parallel-sided ParaPost and tapered Dentatus dowels.