The relationship between water absorption characteristics and the mechanical strength of resin-modified glass-ionomer cements in long-term water storage.

The purpose of this study is to elucidate the water absorption characteristics of resin-modified glass-ionomer cements and to also investigate the relationship between the characteristics and mechanical strength after long-term water storage. The mechanism of water diffusion in these cements is also discussed. Water absorption was measured using a gravimetric analysis for 12 m, while the diffusion coefficient was calculated using Fick's law of diffusion. Water solubility was determined based on the weight of the residue in the immersed water. The compressive and diametral tensile strength were measured at 1, 2, 6, and 12 m. A correlation was observed between the diffusion coefficient and equilibrium water uptake, which thus suggests the water in the cements to diffuse through micro-voids in accordance with the 'Free volumetric theory'. A correlation was seen between the solubility and diffusion coefficient of the cements. The deterioration ratio, defined as the ratio of the strength at 12 m versus that at 1 m, was also calculated. Finally, a negative correlation was observed between the deterioration ratio of the compressive strength and the diffusion coefficients of the cements.