A Segura1, K J Donly, R G Stratmann. 1. Hospital Dentistry, University of Iowa Hospitals and Clinics, Iowa City 52242, USA.
Abstract
PURPOSE: To examine the in vitro remineralization of incipient carious lesions on teeth adjacent interproximally to teeth with Class II glass ionomer cement restorations. MATERIALS AND METHODS: Artificial carious lesions were created at the contact area of 30 teeth. Ten teeth had Class II glass ionomer cement/resin composite restorations placed, 10 teeth had Class II glass ionomer silver cermet restorations placed and 10 teeth had Class II amalgam restorations placed. Sections 100 microns thick were obtained longitudinally through the caries sites and polarized photomicrographs were taken in imbibition media of water and Thoulet's (R.I. 1.41 and 1.47) solutions, representing 5%, 10% and 25% pore volume respectively. Varnish was placed on the section, leaving only the external section site exposed, then sections were situated back into the original tooth. The restored teeth were abutted to the carious tooth so that the restorations came into contact with the adjacent restoration. The specimens were placed into closed environments of artificial saliva for 14 days, then were photographed again under polarized light and areas of the carious lesions were quantitated. RESULTS: An ANOVA indicated significant variance in adjacent tooth remineralization, when comparing the experimental groups, in imbibition media of water (P < 0.05), Thoulet's 1.41 solution (P < 0.008) and Thoulet's 1.47 solution (P < 0.006). Duncan's multiple range test demonstrated the glass ionomer cement/resin composite group to have significantly greater decrease in pore volume (P < 0.05) than the amalgam control group in water imbibition media and Thoulet's 1.47 media. There was no statistically significant difference between the glass ionomer cement/resin composite and glass ionomer silver cermet groups in these two imbibition media. The glass ionomer cement/resin composite group demonstrated significantly more (P < 0.05) decrease in pore volume than both the glass ionomer silver cermet group and amalgam control group in Thoulet's 1.47 imbibition media.
PURPOSE: To examine the in vitro remineralization of incipient carious lesions on teeth adjacent interproximally to teeth with Class II glass ionomer cement restorations. MATERIALS AND METHODS: Artificial carious lesions were created at the contact area of 30 teeth. Ten teeth had Class II glass ionomer cement/resin composite restorations placed, 10 teeth had Class II glass ionomer silver cermet restorations placed and 10 teeth had Class II amalgam restorations placed. Sections 100 microns thick were obtained longitudinally through the caries sites and polarized photomicrographs were taken in imbibition media of water and Thoulet's (R.I. 1.41 and 1.47) solutions, representing 5%, 10% and 25% pore volume respectively. Varnish was placed on the section, leaving only the external section site exposed, then sections were situated back into the original tooth. The restored teeth were abutted to the carious tooth so that the restorations came into contact with the adjacent restoration. The specimens were placed into closed environments of artificial saliva for 14 days, then were photographed again under polarized light and areas of the carious lesions were quantitated. RESULTS: An ANOVA indicated significant variance in adjacent tooth remineralization, when comparing the experimental groups, in imbibition media of water (P < 0.05), Thoulet's 1.41 solution (P < 0.008) and Thoulet's 1.47 solution (P < 0.006). Duncan's multiple range test demonstrated the glass ionomer cement/resin composite group to have significantly greater decrease in pore volume (P < 0.05) than the amalgam control group in water imbibition media and Thoulet's 1.47 media. There was no statistically significant difference between the glass ionomer cement/resin composite and glass ionomer silver cermet groups in these two imbibition media. The glass ionomer cement/resin composite group demonstrated significantly more (P < 0.05) decrease in pore volume than both the glass ionomer silver cermet group and amalgam control group in Thoulet's 1.47 imbibition media.