OBJECTIVES: The short-term fluoride release/uptake of four glass ionomer restoratives was measured and compared to the fluoride release after exposure to three commercial fluoride gels. METHODS: Materials tested were: 1) Ketac-Fil (ESPE GmbH); 2) Ketac-Silver (ESPE GmbH); 3) Photac-Fil (ESPE GmbH); and 4) Fuji II LC (GC Corp.). Twenty discs of each material were fabricated and stored in deionized water at 37 degrees C. Initial fluoride release was measured at 24 h intervals for 7 d, and 24 h intervals at the end of each week for 5 wk. After 6 wk, samples were divided into groups and each group was treated for 6 min with one of the following commercial fluoride gels: acidulated phosphate fluoride (APF), neutral sodium fluoride (NaF), and stannous fluoride (SnF2). Control specimens were placed in deionized water. After exposure, fluoride measurements were carried out at 24 h intervals for 7 d, and 24 h intervals at the end of 2 wk. Fluoride exposure was repeated, and measurements were again recorded over 3 wk. RESULTS: Initial fluoride release by all materials was highest during the first 24 h and decreased sharply over the first week. After exposure to APF, fluoride release increased significantly for all materials. Exposure to NaF also resulted in increased fluoride release for all materials although it was not as high as the increase recorded after exposure to APF. Exposure to SnF2 did not result in significant fluoride release by any material. SIGNIFICANCE: The results of this study suggest that certain fluoride gels may replenish fluoride within some glass ionomers and thus prolong their cariostatic potential.
OBJECTIVES: The short-term fluoride release/uptake of four glass ionomer restoratives was measured and compared to the fluoride release after exposure to three commercial fluoride gels. METHODS: Materials tested were: 1) Ketac-Fil (ESPE GmbH); 2) Ketac-Silver (ESPE GmbH); 3) Photac-Fil (ESPE GmbH); and 4) Fuji II LC (GC Corp.). Twenty discs of each material were fabricated and stored in deionized water at 37 degrees C. Initial fluoride release was measured at 24 h intervals for 7 d, and 24 h intervals at the end of each week for 5 wk. After 6 wk, samples were divided into groups and each group was treated for 6 min with one of the following commercial fluoride gels: acidulated phosphate fluoride (APF), neutral sodium fluoride (NaF), and stannous fluoride (SnF2). Control specimens were placed in deionized water. After exposure, fluoride measurements were carried out at 24 h intervals for 7 d, and 24 h intervals at the end of 2 wk. Fluoride exposure was repeated, and measurements were again recorded over 3 wk. RESULTS: Initial fluoride release by all materials was highest during the first 24 h and decreased sharply over the first week. After exposure to APF, fluoride release increased significantly for all materials. Exposure to NaF also resulted in increased fluoride release for all materials although it was not as high as the increase recorded after exposure to APF. Exposure to SnF2 did not result in significant fluoride release by any material. SIGNIFICANCE: The results of this study suggest that certain fluoride gels may replenish fluoride within some glass ionomers and thus prolong their cariostatic potential.